Vydyne 20NSP BLK is a general-purpose, highly nucleated, lubricated PA66 resin with a further enhanced crystallization temperature. Designed to crystallize rapidly in order to reduce cycle times and increase productivity through faster part set-up.
General
Additive
Lubricant
Features
Fast Molding Cycle, General Purpose, Good Mold Release, Good Stiffness, High Crystallinity, High Rigidity, Lubricated, Nucleated
Agency Rating
ASTM, D4066 PA0131, ASTM, D6779 PA0131, FED, L-P-410A
Automotive Specifications
Toyota TSM5516G, Class 2, Rev 9 (compliance)
UL File Number
E70062
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.14
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.6
*
%
Flow : 23°C, 2.00 mm
1.4
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.2
*
%
Equilibrium, 23°C, 50% RH
2.4
*
%
Outdoor Suitability
f2
UL 746C
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
551144
362595
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
13800
8700
psi
ISO 527-2
Tensile Stress (Break, 23°C)
10900
7250
psi
ISO 527-2
Tensile Strain (Yield, 23°C)
5
15
%
ISO 527-2
Tensile Strain (Break, 23°C)
13
20
%
ISO 527-2
Flexural Modulus (23°C)
464000
189000
psi
ISO 178
Flexural Strength (23°C)
14500
5080
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
2.85
7.14
ftlb/in²
-30°C
2.38
2.38
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
N
N
ftlb/in²
-30°C
N
N
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
2.85
7.14
ftlb/in²
-30°C
2.38
2.38
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
194
-
°F
0.45 MPa, Unannealed
446
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
100
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
100
*
E-6/K
RTI Elec
UL 746
0.400 mm
266
°F
0.710 mm
266
°F
1.50 mm
266
°F
3.00 mm
266
°F
RTI Imp
UL 746
0.400 mm
167
°F
0.710 mm
167
°F
1.50mm
167
°F
3.00 mm
167
°F
RTI Str
UL 746
0.400 mm
167
°F
0.710 mm
185
°F
1.50 mm
185
°F
3.00 mm
185
°F
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E11
-
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
660
-
kV/in
IEC 60243
Arc Resistance (3.00 mm)
5
ASTM D 495
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.400 mm
PLC 1
0.710 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
High Voltage Arc Tracking Rate (HVTR), 3.00 mm
PLC 0
UL 746
Hot-wire Ignition (HWI)
UL 746
0.400 mm
PLC 4
0.710 mm
PLC 4
1.50 mm
PLC 3
3.00 mm
PLC 2
Flammability
dry
cond.
Unit
Test Norm
Flammability
UL 94
0.400 mm
V-2
0.710 mm
V-2
1.50 mm
V-2
3.00 mm
V-2
Glow Wire Flammability Index
IEC 60695-2-12
0.400 mm
1760
°F
0.710 mm
1760
°F
1.50 mm
1760
°F
3.00 mm
1760
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
0.400 mm
1520
°F
0.710 mm
1560
°F
1.50 mm
1560
°F
3.00 mm
1560
°F
Oxygen index
26
*
%
EN ISO 4589-2
Injection
Value
Unit
Drying Temperature
158
°F
Drying Time
1 - 3
h
Rear Temperature
500 - 536
°F
Middle Temperature
518 - 545
°F
Front Temperature
536 - 554
°F
Nozzle temperature
536 - 572
°F
Processing (Melt) Temperature
545 - 572
°F
Mold Temperature
149 - 203
°F