Product Texts
Vydyne 21SPF BLK is a general-purpose, unfilled, lubricated PA66 resin with an enhanced crystallization temperature. Designed principally to decrease cycle time for injection-molding fabrication, this product offers a combination of engineering properties characterized by high strength; rigidity; good toughness; high melt point; good surface lubricity; abrasion resistance; and resistance to many chemicals, machine and motor oils, solvents and gasoline.
General
Additive
Lubricant
Features
Abrasion Resistance, Chemical Resistant, Fast Molding Cycle, Gasoline Resistant, General Purpose, Good Mold Release, Good Toughness, High Rigidity, High Strength, Lubricated, Oil Resistant, Solvent Resistant
Agency Rating
ASTM, D4066 PA0111, ASTM, D6779 PA0111, FED, L-P-410A, MIL, M-20693B, SAE, J1639 PA0121 Z6
Automotive Specifications
Stellantis MS-DB-41 CPN 1948, Toyota TSM5516G, Class 2, Rev 9 (compliance)
UL File Number
E70062
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.14
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
2.0
*
%
Flow : 23°C, 2.00 mm
2.0
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.2
*
%
Equilibrium, 23°C, 50% RH
2.4
*
%
Outdoor Suitability
f2
UL 746C
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
478625
232061
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
12800
7980
psi
ISO 527-2
Tensile Stress (Break, 23°C)
8700
6530
psi
ISO 527-2
Tensile Strain (Yield, 23°C)
5
20
%
ISO 527-2
Tensile Strain (Break, 23°C)
20
>50
%
ISO 527-2
Flexural Modulus (23°C)
479000
152000
psi
ISO 178
Flexural Strength (23°C)
15200
4350
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
2.85
10.9
ftlb/in²
-30°C
2.38
3.33
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
N
N
ftlb/in²
-30°C
N
N
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
2.85
10.9
ftlb/in²
-30°C
2.38
3.33
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
162
-
°F
0.45 MPa, Unannealed
410
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
100
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
100
*
E-6/K
RTI Elec
UL 746
0.400 mm
266
°F
0.710 mm
266
°F
1.50 mm
266
°F
3.00 mm
266
°F
RTI Imp
UL 746
0.400 mm
167
°F
0.710 mm
167
°F
1.50mm
167
°F
3.00 mm
167
°F
RTI Str
UL 746
0.400 mm
167
°F
0.710 mm
185
°F
1.50 mm
185
°F
3.00 mm
185
°F
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E11
-
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
660
-
kV/in
IEC 60243
Arc Resistance (3.00 mm)
5
ASTM D 495
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.400 mm
PLC 1
0.710 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
High Voltage Arc Tracking Rate (HVTR), 3.00 mm
PLC 0
UL 746
Hot-wire Ignition (HWI)
UL 746
0.400 mm
PLC 4
0.710 mm
PLC 4
1.50 mm
PLC 3
3.00 mm
PLC 2
Flammability
dry
cond.
Unit
Test Norm
Flammability
UL 94
0.400 mm
V-2
0.710 mm
V-2
1.50 mm
V-2
3.00 mm
V-2
Glow Wire Flammability Index
IEC 60695-2-12
0.400 mm
1760
°F
0.710 mm
1760
°F
1.50 mm
1760
°F
3.00 mm
1760
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
0.400 mm
1520
°F
0.750 mm
1560
°F
1.50 mm
1560
°F
3.00 mm
1560
°F
Oxygen index
26
*
%
EN ISO 4589-2
Railway Application
dry
cond.
Unit
Test Norm
Oxygen index
26
-
%
EN ISO 4589-2
Injection
Value
Unit
Drying Temperature
158
°F
Drying Time
1 - 3
h
Rear Temperature
500 - 536
°F
Middle Temperature
518 - 545
°F
Front Temperature
536 - 554
°F
Nozzle temperature
536 - 572
°F
Processing (Melt) Temperature
545 - 572
°F
Mold Temperature
149 - 203
°F