Product Texts
Vydyne 22HSPCN NT0856 is a general-purpose, unfilled, lubricated, heat stabilized PA66 resin. Designed principally for injection-molding fabrication, this product offers a combination of engineering properties characterized by high strength; rigidity; good toughness; high melt point; good surface lubricity; abrasion resistance; and resistance to many chemicals, machine and motor oils, solvents and gasoline. This product is designed to resist thermal degradation when exposed to warm climates.
General
Additive
Heat Stabilizer, Lubricant, Release agent
Features
Abrasion Resistance, Chemical Resistant, Gasoline Resistant, General Purpose, Good Heat Resistance, Good Stiffness, Good Strength, Good Tensile Strength, Lubricated, Thermal Stability
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.13
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.7
*
%
Flow : 23°C, 2.00 mm
1.6
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.7
*
%
Equilibrium, 23°C, 50% RH
2.9
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
478625
174046
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
12600
7540
psi
ISO 527-2
Tensile Stress (Break, 23°C)
7980
6670
psi
ISO 527-2
Tensile Strain (Yield, 23°C)
4.9
22
%
ISO 527-2
Tensile Strain (Break, 23°C)
22
>50
%
ISO 527-2
Flexural Modulus (23°C)
435000
145000
psi
ISO 178
Flexural Strength (23°C)
15100
4500
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
2.19
8.56
ftlb/in²
-30°C
2.33
2.24
ftlb/in²
-40°C
1.95
1.9
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
N
N
ftlb/in²
-30°C
N
N
ftlb/in²
-40°C
N
N
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
2.28
9.04
ftlb/in²
-30°C
2.24
2.47
ftlb/in²
-40°C
2.14
2.43
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
153
-
°F
0.45 MPa, Unannealed
390
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
112
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
103
*
E-6/K
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
2.44E15
4.19E10
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
762
584
kV/in
IEC 60243
Injection
Value
Unit
Drying Temperature
158
°F
Drying Time
1 - 3
h
Rear Temperature
500 - 536
°F
Middle Temperature
518 - 545
°F
Front Temperature
536 - 554
°F
Nozzle temperature
536 - 572
°F
Processing (Melt) Temperature
545 - 572
°F
Mold Temperature
149 - 203
°F