Vydyne 41HFE BL0887 is a high impact modified, metal and x-ray detectable, heat stabilized PA66. This resin imparts good toughness and impact resistance while offering metal and x-ray detectability in critical applications.
General
Additive
Heat Stabilizer, Lubricant, Release agent
Features
Heat Stabilized, High Impact Resistance, Lubricated
Appearance
Blue
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.32
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.1
*
%
Flow : 23°C, 2.00 mm
0.8
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.1
*
%
Equilibrium, 23°C, 50% RH
1.1
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
246565
116030
psi
ISO 527-2
Tensile Stress (Break, 23°C)
5510
4640
psi
ISO 527-2
Tensile Strain (Break, 23°C)
33
>50
%
ISO 527-2
Flexural Modulus (23°C)
261000
116000
psi
ISO 178
Flexural Strength (23°C)
6530
2610
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
11.9
22.4
ftlb/in²
-30°C
6.18
5.71
ftlb/in²
-40°C
6.18
5.23
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
N
N
ftlb/in²
-30°C
N
N
ftlb/in²
-40°C
N
N
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
10.5
24.7
ftlb/in²
-30°C
6.18
7.14
ftlb/in²
-40°C
6.18
7.14
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
135
127
°F
0.45 MPa, Unannealed
239
306
°F
Melting Temperature
500
*
°F
ISO 11357-3
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
635
584
kV/in
IEC 60243
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Rear Temperature
536 - 590
°F
Middle Temperature
536 - 590
°F
Front Temperature
536 - 590
°F
Nozzle temperature
536 - 590
°F
Processing (Melt) Temperature
545 - 581
°F
Mold Temperature
149 - 203
°F