Vydyne 65B is a medium-high viscosity resin used for extrusion-compounding. It is desirable to include this neat resin in a formulation in which the melt strength of the final product is critical for the application. Vydyne 65B exhibits good initial color and it has a moisture level below 0.1%. Resistance of Vydyne 65B to heat, oil and wear is typical of PA66 neat resins.
General
Features
Chemical Resistant, Gasoline Resistant, General Purpose, Good Color Stability, Good Toughness, High Rigidity, High Strength, Medium-High Viscosity, Oil Resistant, Solvent Resistant
Uses
Film
Agency Rating
ASTM, D6779 PA0113, FED, L-P-410A, ASTM, D4066 PA0113, EC, 1935/2004, EU, 10/2011, EU, 2023/2006, FDA, 21 CFR 177.1500, MIL, M-20693B
Appearance
Natural Color
Forms
Pellets
Processing Method
Other Extrusion
Physical
dry
cond.
Unit
Test Norm
Density
1.14
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.9
*
%
Flow : 23°C, 2.00 mm
2.0
*
%
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
2.5
*
%
Water Absorption, Saturation, 23°C
8.5
%
ISO 62
Relative Viscosity, Formic Acid
117 - 145
ASTM D 789
Viscosity Number, Sulphuric Acid
6450
*
in³/lb
ISO 307
Moisture Content
0.1
%
ASTM D 6869
Yellowness Index
4
YI
ASTM D 1925
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
449618
217557
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
12000
7980
psi
ISO 527-2
Tensile Stress (Break, 23°C)
7250
9430
psi
ISO 527-2
Tensile Strain (Yield, 23°C)
5.5
20
%
ISO 527-2
Tensile Strain (Break, 23°C)
25
200
%
ISO 527-2
Flexural Modulus (23°C)
406000
102000
psi
ISO 178
Flexural Strength (23°C)
11600
2900
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
2.85
19
ftlb/in²
-30°C
2.85
3.33
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
N
N
ftlb/in²
-30°C
N
N
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
2.85
19
ftlb/in²
-30°C
2.85
3.33
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
149
-
°F
0.45 MPa, Unannealed
383
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
100
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
100
*
E-6/K
Extrusion
Value
Unit
Cylinder Zone 1 Temp
482 - 563
°F
Cylinder Zone 2 Temp
482 - 563
°F
Cylinder Zone 3 Temp
482 - 563
°F
Cylinder Zone 4 Temp
482 - 563
°F
Cylinder Zone 5 Temp
482 - 563
°F
Melt temperature
518 - 563
°F
Die temperature
518 - 563
°F