Vydyne A 1515 GFB BK EST KW2 is standard flow, organic heat stabilized, 15% glass-beads and 15% glass-fiber reinforced PA66 resin. Available in black, this product is also lubricated for improved machine feed and flow. Glass-beads provide the molded parts with good surface finish and low warpage, while glass-fiber increase stiffness and strength.
General
Additive
Heat Stabilizer, Lubricant
Features
Chemical Resistant, Gasoline Resistant, General Purpose, Good Dimensional Stability, Good Flow, Good Heat Resistance, Lubricated, Organic Heat Stabilized
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.35
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.8
*
%
Flow : 23°C, 2.00 mm
0.6
*
%
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
1.7
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
928243
543892
psi
ISO 527-2
Tensile Stress (Break, 23°C)
16000
9860
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.5
5.5
%
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
2.62
4.04
ftlb/in²
ISO 180/1A
Unnotched Izod Impact Strength, +23°C
14.3
21.4
ftlb/in²
ISO 180/1U
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
464
-
°F
0.45 MPa, Unannealed
473
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
Electrical
Value
Unit
Test Norm
Comparative Tracking Index (3.00 mm)
575
V
IEC 60112
Flammability
Value
Unit
Test Norm
Burning Rate, 2.00 mm
102
in/min
ISO 3795
Flammability
UL 94
1.50 mm
HB
3.00 mm
HB
Injection
Value
Unit
Drying Temperature
185 - 203
°F
Drying Time
≥3
h
Rear Temperature
446 - 500
°F
Middle Temperature
446 - 500
°F
Front Temperature
446 - 500
°F
Nozzle temperature
446 - 500
°F
Processing (Melt) Temperature
446 - 500
°F
Mold Temperature
176 - 194
°F