Product Texts
Vydyne A 30 GB NT KW2 is standard flow, organic heat stabilized, 30% glass-beads reinforced PA66 resin. Available in natural, this product is also lubricated for improved machine feed and flow. Glass-beads provide the molded parts with good surface finish and low warpage.
General
Additive
Heat Stabilizer, Lubricant
Features
Chemical Resistant, Gasoline Resistant, General Purpose, Good Dimensional Stability, Good Flow, Good Heat Resistance, Lubricated, Organic Heat Stabilized
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.35
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.2
*
%
Flow : 23°C, 2.00 mm
1.0
*
%
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
1.7
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
652671
362595
psi
ISO 527-2
Tensile Stress (Break, 23°C)
11600
7980
psi
ISO 527-2
Tensile Strain (Break, 23°C)
5
12
%
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
1.9
3.81
ftlb/in²
ISO 180/1A
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
239
-
°F
0.45 MPa, Unannealed
446
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
Electrical
Value
Unit
Test Norm
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
Flammability
Value
Unit
Test Norm
Burning Rate, 2.00 mm
102
in/min
ISO 3795
Flammability
UL 94
1.50 mm
HB
3.00 mm
HB
Injection
Value
Unit
Drying Temperature
185 - 203
°F
Drying Time
≥3
h
Rear Temperature
500 - 554
°F
Middle Temperature
500 - 554
°F
Front Temperature
500 - 554
°F
Nozzle temperature
500 - 554
°F
Processing (Melt) Temperature
500 - 554
°F
Mold Temperature
158 - 194
°F