Vydyne A 30 GF BK WR is standard flow, 30% glass-fiber reinforced PA66 resin. Suitable for use with water up to 85 C, this product is also lubricated for improved machine feed and flow.
General
Additive
Heat Stabilizer, Lubricant
Features
Balanced Stiffness/Toughness, Bromine Free, Chemical Resistant, General Purpose, Good Color Stability, Good Colorability, Good Dimensional Stability, Good Flow, Good Heat Resistance, Good Impact Strength, Good Processability, Good Rigidity, Good Strength, Good Tensile Strength, Halogen Content, None, Heat Aging Resistant, Heat Stabilized, Homopolymer, Hydrolysis Resistant, Lubricated, Medium Viscosity, Non-Corrosive, Thermal Stability
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.36
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.7
*
%
Flow : 23°C, 2.00 mm
0.3
*
%
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
1.7
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.33E6
-
psi
ISO 527-2
Tensile Stress (Break, 23°C)
23200
-
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.5
-
%
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
5.23
-
ftlb/in²
ISO 180/1A
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
464
-
°F
0.45 MPa, Unannealed
491
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
Electrical
Value
Unit
Test Norm
Comparative Tracking Index (3.00 mm)
575
V
IEC 60112
Flammability
Value
Unit
Test Norm
Flammability
UL 94
1.60 mm
HB
3.20 mm
HB
Glow Wire Flammability Index
IEC 60695-2-12
2.00 mm
1200
°F
Injection
Value
Unit
Drying Temperature
176 - 230
°F
Drying Time
3 - 4
h
Rear Temperature
518 - 563
°F
Middle Temperature
527 - 563
°F
Front Temperature
536 - 572
°F
Nozzle temperature
536 - 572
°F
Processing (Melt) Temperature
536 - 563
°F
Mold Temperature
158 - 203
°F