Product Texts
Vydyne A/B 15 GF BK KW EM is standard flow, organic heat stabilized, low impact modified 15% glass-fiber reinforced PA66/PA6 resin. Available in black, this product is specifically designed for blow molding applications.
General
Additive
Heat Stabilizer, Lubricant
Features
Chemical Resistant, Gasoline Resistant, General Purpose, Good Flow, Good Heat Resistance, Impact Modified, Lubricated, Organic Heat Stabilized
Uses
Impact Modified
Appearance
Black
Forms
Pellets
Processing Method
Blow Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.22
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.3
*
%
Flow : 23°C, 2.00 mm
0.3
*
%
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
1.8
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
797709
507633
psi
ISO 527-2
Tensile Stress (Break, 23°C)
16700
10200
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3
4.5
%
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
5.23
9.51
ftlb/in²
ISO 180/1A
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
410
-
°F
0.45 MPa, Unannealed
446
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
Electrical
Value
Unit
Test Norm
Comparative Tracking Index (3.00 mm)
550
V
IEC 60112
Flammability
Value
Test Norm
Flammability
UL 94
0.750 mm
HB
1.50 mm
HB
3.00 mm
HB
Injection
Value
Unit
Drying Temperature
176 - 212
°F
Drying Time
≥3
h
Rear Temperature
491 - 554
°F
Middle Temperature
491 - 554
°F
Front Temperature
491 - 554
°F
Nozzle temperature
491 - 554
°F
Processing (Melt) Temperature
491 - 554
°F
Mold Temperature
158 - 194
°F