Vydyne AG10K is a 50% glass fiber reinforced, heat and hydrolytically stabilized PA66 for injection molded applications.
General
Additive
Heat Stabilizer, Release agent
Features
Good Strength, Outstanding Surface Finish
Certifications
Drinking water contact, Drinking water contact KTW, Drinking water contact DVGW W270, Drinking water contact NSF
Appearance
Natural Color, Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.55
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.7
*
%
Flow : 23°C, 2.00 mm
0.3
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.8
*
%
Equilibrium, 23°C, 50% RH
1.2
*
%
Water Absorption, Saturation, 23°C
2.5
%
ISO 62
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
2.28E6
1.81E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
31800
23900
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.6
3.5
%
ISO 527-2
Flexural Modulus (23°C)
2.34E6
1.71E6
psi
ISO 178
Flexural Strength (23°C)
48600
34800
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
6.66
8.56
ftlb/in²
-30°C
6.66
6.18
ftlb/in²
-40°C
7.14
5.71
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
42.3
46.1
ftlb/in²
-30°C
39.5
39.5
ftlb/in²
-40°C
39.5
37.6
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
6.66
8.09
ftlb/in²
-30°C
6.18
6.18
ftlb/in²
-40°C
5.23
5.71
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
487
-
°F
0.45 MPa, Unannealed
502
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
RTI Elec
UL 746
0.750 mm
149
°F
3.00 mm
149
°F
RTI Imp
UL 746
0.750 mm
149
°F
3.00 mm
149
°F
RTI Str
UL 746
0.750 mm
149
°F
3.00 mm
149
°F
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E14
-
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
660
610
kV/in
IEC 60243
Flammability
Value
Test Norm
Flammability
UL 94
0.750 mm
HB
3.00 mm
HB
Injection
Value
Unit
Drying Temperature
167 - 185
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
500 - 536
°F
Middle Temperature
518 - 536
°F
Front Temperature
518 - 554
°F
Processing (Melt) Temperature
518 - 554
°F
Mold Temperature
140 - 194
°F