Vydyne AVS4CC1 BK0888 is part of Ascend's Anti-Vibration System portfolio. AVS4CC1 BK0888 is a 35% glass filled specialty compound that is specifically designed to provide an improvement in damping performance for critical NVH components without sacrificing the mechanical stiffness.
General
Additive
Heat Stabilizer, Lubricant
Features
Fatigue Resistant, Good Stiffness, Good Strength, Good Tensile Strength, Heat Stabilized, Lubricated
Uses
Glass Reinforced
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.42
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.8
*
%
Flow : 23°C, 2.00 mm
0.3
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.1
*
%
Equilibrium, 23°C, 50% RH
1.7
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.67E6
1.35E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
28900
20200
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.7
4
%
ISO 527-2
Flexural Modulus (23°C)
1.62E6
1.28E6
psi
ISO 178
Flexural Strength (23°C)
42400
28700
psi
ISO 178
Poisson's Ratio (23°C)
0.34
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
5.23
5.71
ftlb/in²
-30°C
4.76
4.33
ftlb/in²
-40°C
4.52
4.19
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
36.6
37.6
ftlb/in²
-30°C
30.4
28.5
ftlb/in²
-40°C
30
27.6
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
5.23
5.71
ftlb/in²
-30°C
4.52
4.33
ftlb/in²
-40°C
4.52
4.19
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
477
464
°F
0.45 MPa, Unannealed
500
495
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
21
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
85
*
E-6/K
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
686
660
kV/in
IEC 60243
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
0.15
%
Rear Temperature
536 - 590
°F
Middle Temperature
536 - 590
°F
Front Temperature
536 - 590
°F
Nozzle temperature
536 - 590
°F
Processing (Melt) Temperature
545 - 581
°F
Mold Temperature
149 - 203
°F
Applications
EV Motor Mount, EV AC Bracket, Engine Mount
Powertrain