Vydyne ECO515H NT0867 is a non-halogenated flame retardant, 15% glass fiber, heat stabilized PA66. ECO515H NT0867 has improved stiffness and strength.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Lubricant
Features
Corrosion Resistant, Electrical Corrosion Resistant, Fast Molding Cycle, Flame Retardant, Good Colorability, Good Dimensional Stability, Good Electrical Properties, Good Processability, Good Strength, Heat Aging Resistant, Heat Stabilized, High Flow, Low Density, Lubricated
Uses
Flame Retardant, Glass Reinforced
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.32
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.8
*
%
Flow : 23°C, 2.00 mm
0.4
*
%
Water Absorption
ISO 62
23°C, 24 hr
2.1
*
%
Equilibrium, 23°C, 50% RH
1.7
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
971755
652671
psi
ISO 527-2
Tensile Stress (Break, 23°C)
14500
9570
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3.2
5.5
%
ISO 527-2
Flexural Modulus (23°C)
972000
624000
psi
ISO 178
Flexural Strength (23°C)
23200
12000
psi
ISO 178
Poisson's Ratio (23°C)
0.36
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
3.95
4.76
ftlb/in²
-30°C
2.95
2.81
ftlb/in²
-40°C
2.9
2.81
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
25.7
28.1
ftlb/in²
-30°C
25.2
23.3
ftlb/in²
-40°C
25.2
23.3
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
3.43
4.61
ftlb/in²
-30°C
3.43
3.04
ftlb/in²
-40°C
3
3
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
432
421
°F
0.45 MPa, Unannealed
482
477
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
30
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
87
*
E-6/K
RTI Elec
UL 746
0.200 mm
284
°F
0.400 mm
284
°F
0.750 mm
284
°F
1.50 mm
284
°F
3.00 mm
284
°F
RTI Imp
UL 746
0.200 mm
230
°F
0.400 mm
239
°F
0.750 mm
266
°F
1.50mm
266
°F
3.00 mm
284
°F
RTI Str
UL 746
0.200 mm
248
°F
0.400 mm
257
°F
0.750 mm
284
°F
1.50 mm
284
°F
3.00 mm
302
°F
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
762
686
kV/in
IEC 60243
High Amp Arc Ignition (HAI)
UL 746
0.400 mm
PLC 0
0.750 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
Hot-wire Ignition (HWI)
UL 746
0.750 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
Flammability
Value
Test Norm
Flammability
UL 94
0.200 mm
V-0
0.400 mm
V-0
0.750 mm
V-0
1.50 mm
V-0
3.00 mm
V-0
Flammability, 5V
UL 94
1.50 mm
5VA
3.00 mm
5VA
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4 - 6
h
Suggested Max Regrind
50
%
Suggested Max Moisture
≤0.2
%
Rear Temperature
527 - 572
°F
Middle Temperature
527 - 572
°F
Front Temperature
527 - 572
°F
Nozzle temperature
527 - 572
°F
Processing (Melt) Temperature
527 - 572
°F
Mold Temperature
140 - 248
°F