Product Texts
Vydyne LUB A 30 FC BK TF13 SI KW is standard flow 30% carbon-fiber reinforced, 13% PTFE 1% silicone lubricated PA66 resin. Available in black, it is specifically designed for high stiffness and strength. This product also has a low coefficient of friction and is electrically conductive.
General
Additive
Heat Stabilizer, Lubricant
Features
Abrasion Resistance, Chemical Resistant, Gasoline Resistant, General Purpose, Good Flow, Good Stiffness, High Tensile Strength, Lubricated, Organic Heat Stabilized, Slip
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.35
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.3
*
%
Flow : 23°C, 2.00 mm
0.1
*
%
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
1.7
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
2.97E6
2.23E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
29700
23200
psi
ISO 527-2
Tensile Strain (Break, 23°C)
1.5
3
%
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
4.28
5.71
ftlb/in²
ISO 180/1A
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
473
-
°F
0.45 MPa, Unannealed
482
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
100
-
Ohm*m
IEC 60093
Flammability
Value
Test Norm
Flammability
UL 94
1.50 mm
HB
3.00 mm
HB
Injection
Value
Unit
Drying Temperature
194 - 230
°F
Drying Time
≥3
h
Rear Temperature
518 - 536
°F
Middle Temperature
518 - 563
°F
Front Temperature
518 - 563
°F
Nozzle temperature
518 - 563
°F
Processing (Melt) Temperature
518 - 563
°F
Mold Temperature
158 - 194
°F