Product Texts
Vydyne R633H05 is 33% glass-fiber reinforced PA66/6 copolymer resin for superior surface appearance. Available in black, this injection-molding grade resin is lubricated for machine feed and mold release.
General
Additive
Heat Stabilizer, Lubricant
Features
Copolymer, Good Mold Release, Good Surface Finish, Heat Stabilized, High Tensile Strength, Lubricated
Uses
Glass Reinforced
Agency Rating
ASTM, D4066 PA112G35, ASTM, D6779 PA082G35, FED, L-P-410A, SAE, J1639 PA1816 Z6
Automotive Specifications
Stellantis MS-DB-41 CPN 4005
UL File Number
E70062
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.39
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.9
*
%
Flow : 23°C, 2.00 mm
0.4
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.3
*
%
Equilibrium, 23°C, 50% RH
2.3
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.57E6
1.16E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
26700
18900
psi
ISO 527-2
Tensile Strain (Break, 23°C)
4
6
%
ISO 527-2
Flexural Modulus (23°C)
1.28E6
986000
psi
ISO 178
Flexural Strength (23°C)
37000
28300
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
5.71
11.9
ftlb/in²
-30°C
5.23
7.14
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
24.3
43.8
ftlb/in²
-30°C
20.9
43.3
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
6.18
10.5
ftlb/in²
-30°C
5.71
9.04
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
428
-
°F
0.45 MPa, Unannealed
446
-
°F
Melting Temperature
451
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
15
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
100
*
E-6/K
Electrical
Value
Unit
Test Norm
Arc Resistance (3.00 mm)
5
ASTM D 495
Comparative Tracking Index (3.00 mm)
250 - 399
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.750 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
High Voltage Arc Tracking Rate (HVTR), 3.00 mm
PLC 2
UL 746
Hot-wire Ignition (HWI)
UL 746
0.750 mm
PLC 4
1.50 mm
PLC 4
3.00 mm
PLC 3
Flammability
Value
Test Norm
Flammability
UL 94
0.750 mm
HB
1.50 mm
HB
3.00 mm
HB
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Rear Temperature
536 - 590
°F
Middle Temperature
536 - 590
°F
Front Temperature
536 - 590
°F
Nozzle temperature
536 - 590
°F
Processing (Melt) Temperature
545 - 581
°F
Mold Temperature
149 - 203
°F