Product Texts
Vydyne R530H BK02 is a general purpose, 30% glass-filled, heat-stabilized PA66 based resin designed for injection molding applications. R530H BK02 offers improved flow with a black surface finish and maintains the excellent resistance typical of PA66 in chemicals, machine and motor oils, solvents, and gasoline.
General
Additive
Heat Stabilizer, Lubricant
Features
Antifreeze Resistant, Chemical Resistant, Fatigue Resistant, Gasoline Resistant, Heat Stabilized, High Flow, Hydrolysis Resistant, Lubricated, Solvent Resistant
Uses
Glass Reinforced
Agency Rating
ASTM, D4066 PA012G30, ASTM, D6779 PA012G30
Automotive Specifications
Aisin TO20141124 - P-PA66-GF30-807, Chery Motor Q-SQR.S1-33-2012 CMP.PA66.G6, Ford WSS-M4D752-B1 , GM GMW16270P-PA66-GF30, GM GMW3038P-PA66-GF30H, GM GMW3038P-PA66-GF30J, Mahle SD2-181 (AR.06576) Rev. 7, Mahle SD2-181 (AR.06576) Rev. 7, Modine GM2055, Stellantis MS-DB-41 CPN 4018, Toyota TSM5603G, Class 2B, Rev 5 (compliance), Valeo NVB 15007 Class 2B, Valeo NVB 15007 Class 3A, Valeo NVB 15008 Class 3
UL File Number
E70062
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.37
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.9
*
%
Flow : 23°C, 2.00 mm
0.4
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.9
*
%
Equilibrium, 23°C, 50% RH
1.9
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.45E6
1.07E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
28300
18300
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3
5
%
ISO 527-2
Flexural Modulus (23°C)
1.39E6
986000
psi
ISO 178
Flexural Strength (23°C)
39200
24700
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
5.23
6.18
ftlb/in²
-30°C
4.52
4.76
ftlb/in²
-40°C
4.28
4.52
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
35.7
42.8
ftlb/in²
-30°C
30.9
34.3
ftlb/in²
-40°C
30.9
34.3
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
5.23
6.18
ftlb/in²
-30°C
4.76
5.23
ftlb/in²
-40°C
4.52
4.76
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
482
-
°F
0.45 MPa, Unannealed
500
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
22
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
110
*
E-6/K
RTI Elec
UL 746
0.750 mm
284
°F
1.50 mm
284
°F
3.00 mm
284
°F
RTI Imp
UL 746
0.750 mm
248
°F
1.50mm
248
°F
3.00 mm
248
°F
RTI Str
UL 746
0.750 mm
257
°F
1.50 mm
284
°F
3.00 mm
284
°F
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E11
-
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
787
508
kV/in
IEC 60243
Arc Resistance (3.00 mm)
6
ASTM D 495
Comparative Tracking Index (3.00 mm)
250 - 399
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.750 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
High Voltage Arc Tracking Rate (HVTR), 3.00 mm
PLC 1
UL 746
Hot-wire Ignition (HWI)
UL 746
0.750 mm
PLC 4
1.50 mm
PLC 3
3.00 mm
PLC 4
Flammability
Value
Unit
Test Norm
Burning Rate, 2.00 mm
0
in/min
ISO 3795
Flammability
UL 94
0.750 mm
HB
1.50 mm
HB
3.00 mm
HB
Glow Wire Flammability Index
IEC 60695-2-12
0.750 mm
1250
°F
1.50 mm
1250
°F
3.00 mm
1250
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
0.750 mm
1290
°F
1.50 mm
1290
°F
3.00 mm
1290
°F
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Rear Temperature
536 - 590
°F
Middle Temperature
536 - 590
°F
Front Temperature
536 - 590
°F
Nozzle temperature
536 - 590
°F
Processing (Melt) Temperature
545 - 581
°F
Mold Temperature
149 - 203
°F