Product Texts
Vydyne R530H NT is a general purpose, 30% glass-filled, heat-stabilized PA66 based resin designed for injection molding applications. R530H NT offers improved flow with a natural surface finish and maintains the excellent resistance typical of PA66 in chemicals, machine and motor oils, solvents, and gasoline.
General
Additive
Heat Stabilizer, Lubricant
Features
Antifreeze Resistant, Chemical Resistant, Fatigue Resistant, Gasoline Resistant, Good Flow, Heat Stabilized, Lubricated, Solvent Resistant
Uses
Glass Reinforced
Agency Rating
ASTM, D4066 PA012G30, ASTM, D6779 PA012G30, FDA, 21 CFR 177.1500, EU, 2023/2006, EU, 10/2011, EC, 1935/2004
Automotive Specifications
GM GMW3038P-PA66-GF30J, Tesla TM-1006 v3 - 301130, Tesla TM-1006 v3 - 201130, Tesla TM-1006 v3 - 101130, Stellantis MS-DB-41 CPN 4818, Mahle SD2-181 (AR.06576) Rev. 7, Mahle SD2-181 (AR.06576) Rev. 7, HMG MS211-42 Type A, GM GMW3038P-PA66-GF30H, GM GMW16270P-PA66-GF30, Ford WSS-M4D752-B1 , Chery Motor Q-SQR.S1-33-2012 CMP.PA66.G6, Aisin TO20141124 - P-PA66-GF30-807, Toyota TSM5603G, Class 2B, Rev 5 (compliance)
UL File Number
E70062
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.37
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.2
*
%
Flow : 23°C, 2.00 mm
0.5
*
%
Water Absorption, 23°C, 24 hr
1.2
*
%
ISO 62
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.45E6
1.07E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
28300
19600
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3
5
%
ISO 527-2
Flexural Modulus (23°C)
1.38E6
1.17E6
psi
ISO 178
Flexural Strength (23°C)
39500
30200
psi
ISO 178
Poisson's Ratio (23°C)
0.37
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
6.18
6.66
ftlb/in²
-30°C
5.71
5.23
ftlb/in²
-40°C
5.71
5.23
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
34.3
42.8
ftlb/in²
-30°C
30
31.9
ftlb/in²
-40°C
29
30.4
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
5.23
6.18
ftlb/in²
-30°C
5.23
5.23
ftlb/in²
-40°C
5.23
5.23
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
486
482
°F
0.45 MPa, Unannealed
504
502
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
22
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
76
*
E-6/K
RTI Elec
UL 746
0.750 mm
284
°F
1.50 mm
284
°F
3.00 mm
284
°F
RTI Imp
UL 746
0.750 mm
248
°F
1.50mm
248
°F
3.00 mm
248
°F
RTI Str
UL 746
0.750 mm
257
°F
1.50 mm
284
°F
3.00 mm
284
°F
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E11
-
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
508
-
kV/in
IEC 60243
Arc Resistance (3.00 mm)
6
ASTM D 495
Comparative Tracking Index (3.00 mm)
250 - 399
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.750 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
High Voltage Arc Tracking Rate (HVTR), 3.00 mm
PLC 1
UL 746
Hot-wire Ignition (HWI)
UL 746
0.750 mm
PLC 4
1.50 mm
PLC 3
3.00 mm
PLC 4
Flammability
Value
Unit
Test Norm
Burning Rate, 2.00 mm
0
in/min
ISO 3795
Flammability
UL 94
0.750 mm
HB
1.50 mm
HB
3.00 mm
HB
Glow Wire Flammability Index
IEC 60695-2-12
0.750 mm
1250
°F
1.50 mm
1250
°F
3.00 mm
1250
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
0.750 mm
1290
°F
1.50 mm
1290
°F
3.00 mm
1290
°F
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Rear Temperature
536 - 590
°F
Middle Temperature
536 - 590
°F
Front Temperature
536 - 590
°F
Nozzle temperature
536 - 590
°F
Processing (Melt) Temperature
545 - 581
°F
Mold Temperature
149 - 203
°F
Applications
Auxiliary Coolant Heaters
Vehicles
Auxiliary Air Heaters
Vehicles