Product Texts
Vydyne R535HT BK653 is a 35% glass-filled, heat-stabilized PA66+PA6 based resin designed for injection molding applications. It was specifically developed to withstand long term exposure to elevated temperatures up to 190°C. R535HT BK653 offers improved flow with an improved black surface finish and maintains the excellent resistance typical of PA66 in chemicals, machine and motor oils, solvents, and gasoline.
General
Additive
Heat Stabilizer, Lubricant
Features
Antifreeze Resistant, Chemical Resistant, Fatigue Resistant, Gasoline Resistant, Heat Stabilized, High Flow, Lubricated, Solvent Resistant
Uses
Glass Reinforced
Agency Rating
ASTM, D4066 PA114G35, ASTM, D6779 PA084G35
Automotive Specifications
GM GMW17961P-PA-GF35-T1, Mercedes-Benz DBL 5408 (compliance), Renault AS23a, Renault UB02d, Stellantis 01994_18_00678, VW VW50133 (compliance)
UL File Number
E70062
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.42
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.9
*
%
Flow : 23°C, 2.00 mm
0.4
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.8
*
%
Equilibrium, 23°C, 50% RH
1.6
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.58E6
1.04E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
29700
18100
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3.1
7.6
%
ISO 527-2
Flexural Modulus (23°C)
1.48E6
914000
psi
ISO 178
Flexural Strength (23°C)
40600
21000
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
5.71
8.56
ftlb/in²
-30°C
5.23
5.71
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
35.7
40.4
ftlb/in²
-30°C
30.9
35.7
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
6.66
8.56
ftlb/in²
-30°C
6.18
6.18
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
464
-
°F
0.45 MPa, Unannealed
493
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
19
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
81.4
*
E-6/K
Flammability
Value
Unit
Test Norm
Burning Rate, 2.00 mm
0
in/min
ISO 3795
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Rear Temperature
536 - 590
°F
Middle Temperature
536 - 590
°F
Front Temperature
536 - 590
°F
Nozzle temperature
536 - 590
°F
Processing (Melt) Temperature
545 - 581
°F
Mold Temperature
149 - 203
°F
Applications
Charge Air Cooler End Tank
Cooling Systems
Turbo Duct
Cooling Systems