Product Texts
Vydyne STAT A 12 FC BK is standard flow 12% carbon-fiber reinforced PA66 resin. Available in black, it is specifically designed for high stiffness and strength. This product is also electrically dissipative.
General
Additive
Lubricant
Features
Chemical Resistant, Gasoline Resistant, General Purpose, Good Dimensional Stability, Good Flow, Good Stiffness, High Tensile Strength, Lubricated
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.19
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.0
*
%
Flow : 23°C, 2.00 mm
0.5
*
%
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
2.3
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.31E6
913739
psi
ISO 527-2
Tensile Stress (Break, 23°C)
21000
14500
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3.5
6
%
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
3.33
5.71
ftlb/in²
ISO 180/1A
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
455
-
°F
0.45 MPa, Unannealed
473
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
10000
-
Ohm*m
IEC 60093
Flammability
Value
Test Norm
Flammability
UL 94
1.50 mm
HB
3.00 mm
HB
Injection
Value
Unit
Drying Temperature
194 - 230
°F
Drying Time
≥3
h
Rear Temperature
518 - 536
°F
Middle Temperature
518 - 563
°F
Front Temperature
518 - 563
°F
Nozzle temperature
518 - 563
°F
Processing (Melt) Temperature
518 - 563
°F
Mold Temperature
158 - 194
°F