Vydyne STAT A 20 FC BK is standard flow, 20% carbon-fiber reinforced PA66 resin. This product shows high stiffness and strength. It is also electrically conductive.
General
Additive
Lubricant
Features
Bromine Free, Chemical Resistant, General Purpose, Good Dimensional Stability, Good Electrical Properties, Good Processability, Good Rigidity, Good Stiffness, Good Strength, Good Tensile Strength, Halogen Content, None, Homopolymer, Lubricated, Medium Viscosity, Non-Corrosive, Oil Resistant
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.22
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.4
*
%
Flow : 23°C, 2.00 mm
0.2
*
%
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
2.1
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.89E6
-
psi
ISO 527-2
Tensile Stress (Break, 23°C)
23200
-
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2
-
%
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
3.81
-
ftlb/in²
ISO 180/1A
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
473
-
°F
0.45 MPa, Unannealed
491
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
10
-
Ohm*m
IEC 60093
Flammability
Value
Test Norm
Flammability
UL 94
0.800 mm
HB
1.50 mm
HB
3.20 mm
HB
Injection
Value
Unit
Drying Temperature
176 - 230
°F
Drying Time
3 - 4
h
Rear Temperature
518 - 563
°F
Middle Temperature
527 - 563
°F
Front Temperature
536 - 572
°F
Nozzle temperature
536 - 572
°F
Processing (Melt) Temperature
536 - 563
°F
Mold Temperature
158 - 194
°F