Product Texts
Vydyne B 30 GF BK EST K1 is standard flow, heat stabilized, 30% glass-fiber reinforced PA6 resin. Available in black, this product is also lubricated for improved machine feed and flow.
General
Additive
Heat Stabilizer, Lubricant
Features
Chemical Resistant, Gasoline Resistant, General Purpose, Good Flow, High Heat Resistance, Lubricated
Uses
Glass Reinforced
Automotive Specifications
Renault AS21
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.35
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.7
*
%
Flow : 23°C, 2.00 mm
0.3
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.3
*
%
Equilibrium, 23°C, 50% RH
1.9
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.33E6
870228
psi
ISO 527-2
Tensile Stress (Break, 23°C)
24700
15200
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3
6.5
%
ISO 527-2
Flexural Modulus (23°C)
1.49E6
827000
psi
ISO 178
Flexural Strength (23°C)
35500
19600
psi
ISO 178
Poisson's Ratio (23°C)
0.35
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
6.66
9.51
ftlb/in²
-30°C
6.66
5.23
ftlb/in²
-40°C
4.61
4.42
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
42.3
47.1
ftlb/in²
-30°C
35.7
43.3
ftlb/in²
-40°C
35.7
36.2
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
6.18
9.99
ftlb/in²
-30°C
5.23
5.71
ftlb/in²
-40°C
4.42
4.76
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
405
387
°F
0.45 MPa, Unannealed
428
426
°F
Melting Temperature
428
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
23
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
84
*
E-6/K
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
711
660
kV/in
IEC 60243
Comparative Tracking Index (3.00 mm)
450
V
IEC 60112
Flammability
Value
Test Norm
Flammability
UL 94
1.50 mm
HB
3.00 mm
HB
Injection
Value
Unit
Drying Temperature
194 - 212
°F
Drying Time
≥3
h
Rear Temperature
446 - 536
°F
Middle Temperature
446 - 536
°F
Front Temperature
446 - 536
°F
Nozzle temperature
446 - 536
°F
Processing (Melt) Temperature
446 - 536
°F
Mold Temperature
176 - 194
°F