Product Texts
Vydyne B 30 GF BK G/W is a standard flow, 30% glass-fiber reinforced PA 6 resin. This product is also lubricated to improve machine feed and flow. It is suitable for high-thickness parts.
General
Additive
Lubricant
Features
Balanced Stiffness/Toughness, Bromine Free, Chemical Resistant, Fast Molding Cycle, General Purpose, Good Color Stability, Good Impact Strength, Good Mold Release, Good Processability, Good Rigidity, Good Stiffness, Good Strength, Good Surface Finish, Good Tensile Strength, Good Toughness, Halogen Content, None, High Crystallinity, High Flow, Homopolymer, Low Viscosity, Lubricated, Non-Corrosive, Nucleated, Thermal Stability
Uses
Glass Reinforced
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.35
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.8
*
%
Flow : 23°C, 2.00 mm
0.4
*
%
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
2.1
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.28E6
-
psi
ISO 527-2
Tensile Stress (Break, 23°C)
23200
-
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.5
-
%
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
4.28
-
ftlb/in²
ISO 180/1A
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
401
-
°F
0.45 MPa, Unannealed
419
-
°F
Melting Temperature
428
*
°F
ISO 11357-3
Electrical
Value
Unit
Test Norm
Comparative Tracking Index (3.00 mm)
575
V
IEC 60112
Flammability
Value
Unit
Test Norm
Flammability
UL 94
1.60 mm
HB
3.20 mm
HB
Glow Wire Flammability Index
IEC 60695-2-12
2.00 mm
1200
°F
Injection
Value
Unit
Drying Temperature
176 - 230
°F
Drying Time
3 - 4
h
Rear Temperature
446 - 491
°F
Middle Temperature
455 - 500
°F
Front Temperature
464 - 500
°F
Nozzle temperature
464 - 500
°F
Processing (Melt) Temperature
464 - 500
°F
Mold Temperature
158 - 203
°F