Product Texts
Vydyne B 30 GF H BK0947 is a laser markable, heat stabilized, and 30% glass reinforced PA6. This product is also lubricated for improved machine feed and flow, suitable for injection molding applications.
General
Additive
Heat Stabilizer, Lubricant, Release agent
Features
Good Flow, Heat Aging Resistant, Laser Markable, Lubricated
Uses
Glass Reinforced
Automotive Specifications
Stellantis MS-DB-41 CPN 3840
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.37
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.6
*
%
Flow : 23°C, 2.00 mm
0.3
*
%
Water Absorption
ISO 62
23°C, 24 hr
2
*
%
Equilibrium, 23°C, 50% RH
2.1
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.41E6
899236
psi
ISO 527-2
Tensile Stress (Break, 23°C)
25100
15800
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3.4
8.5
%
ISO 527-2
Flexural Modulus (23°C)
1.33E6
783000
psi
ISO 178
Flexural Strength (23°C)
36000
19000
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
5.23
9.99
ftlb/in²
-30°C
4.47
5.23
ftlb/in²
-40°C
4.42
4.71
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
37.6
49.5
ftlb/in²
-30°C
32.8
35.2
ftlb/in²
-40°C
32.8
34.3
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
5.23
9.51
ftlb/in²
-30°C
4.52
5.71
ftlb/in²
-40°C
4.38
5.23
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
397
385
°F
0.45 MPa, Unannealed
424
424
°F
Melting Temperature
428
*
°F
ISO 11357-3
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
686
356
kV/in
IEC 60243
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4 - 12
h
Suggested Max Regrind
25
%
Rear Temperature
446 - 491
°F
Middle Temperature
455 - 500
°F
Front Temperature
464 - 500
°F
Nozzle temperature
464 - 500
°F
Processing (Melt) Temperature
464 - 500
°F
Mold Temperature
158 - 203
°F