Vydyne B 35 GF NT is standard flow, 35% glass-fiber reinforced PA6 resin. Available in natural, this product is also lubricated for improved machine feed and flow.
General
Additive
Lubricant
Features
Chemical Resistant, Gasoline Resistant, General Purpose, Good Flow, Good Heat Resistance, Lubricated
Uses
Glass Reinforced
Appearance
Natural Color, Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.41
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.6
*
%
Flow : 23°C, 2.00 mm
0.3
*
%
Water Absorption
ISO 62
23°C, 24 hr
1
*
%
Equilibrium, 23°C, 50% RH
2
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.6E6
-
psi
ISO 527-2
Tensile Stress (Break, 23°C)
28000
-
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.9
-
%
ISO 527-2
Flexural Modulus (23°C)
1.41E6
-
psi
ISO 178
Flexural Strength (23°C)
42100
-
psi
ISO 178
Poisson's Ratio (23°C)
0.34
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
8.56
-
ftlb/in²
-30°C
6.18
-
ftlb/in²
-40°C
5.23
-
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
45.2
-
ftlb/in²
-30°C
40.4
-
ftlb/in²
-40°C
35.7
-
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
7.37
-
ftlb/in²
-30°C
5.47
-
ftlb/in²
-40°C
4.76
-
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
410
-
°F
0.45 MPa, Unannealed
419
-
°F
Melting Temperature
428
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
18
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
65
*
E-6/K
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
635
-
kV/in
IEC 60243
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
Flammability
Value
Unit
Test Norm
Burning Rate, 2.00 mm
102
in/min
ISO 3795
Glow Wire Flammability Index
IEC 60695-2-12
2.00 mm
1200
°F
Injection
Value
Unit
Drying Temperature
176 - 194
°F
Drying Time
≥3
h
Processing (Melt) Temperature
446 - 500
°F
Mold Temperature
176 - 194
°F