Product Texts
Vydyne B BK X146 EM2 LT K1 is a general-purpose, impact-modified PA6 resin. Available in black, it is inorganic heat-stabilized for improved resistance to high temperatures. It is lubricated for machine feed and easy mold release and shows a high impact resistance also at low temperatures.
General
Additive
Heat Stabilizer, Lubricant
Features
Abrasion Resistance, Chemical Resistant, Gasoline Resistant, Good Mold Release, Good Toughness, Heat Aging Resistant, High Elongation, Impact Modified, Low Temperature Impact Resistance, Lubricated, Oil Resistant, Solvent Resistant
Uses
Impact Modified
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.10
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.9
*
%
Flow : 23°C, 2.00 mm
1.6
*
%
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
2.5
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
348091
232061
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
8990
5800
psi
ISO 527-2
Tensile Strain (Yield, 23°C)
6
10
%
ISO 527-2
Tensile Strain (Break, 23°C)
55
65
%
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength
ISO 180/1A
+23°C
9.51
-
ftlb/in²
-30°C
5.71
-
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
140
-
°F
0.45 MPa, Unannealed
293
-
°F
Melting Temperature
432
*
°F
ISO 11357-3
Electrical
Value
Unit
Test Norm
Comparative Tracking Index (3.00 mm)
450
V
IEC 60112
Flammability
Value
Test Norm
Flammability
UL 94
0.750 mm
HB
1.50 mm
HB
Injection
Value
Unit
Drying Temperature
176 - 194
°F
Drying Time
≥3
h
Rear Temperature
446 - 518
°F
Middle Temperature
446 - 518
°F
Front Temperature
446 - 518
°F
Nozzle temperature
446 - 518
°F
Processing (Melt) Temperature
446 - 518
°F
Mold Temperature
176 - 194
°F