Product Texts
Starflam 366 (formerly Vydyne® ECO366) is a non-halogenated, unreinforced, flame-retardant PA66 compound designed with high comparative tracking index (CTI) and low corrosion for improved electrical contact performance. It has superior flow properties to assist in filling thin-walled, intricate parts with reduced warpage and reduced cycle time. It is lubricated for machine feed and easy mold release.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Lubricant
Features
Crack Resistant, Flame Retardant, Good Mold Release, Good Toughness, Halogen Content, None, Low Density, Lubricated, Organic Heat Stabilized
Uses
Flame Retardant
UL File Number
E70062
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.17
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.2
*
%
Flow : 23°C, 2.00 mm
0.9
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.8
*
%
Equilibrium, 23°C, 50% RH
2.3
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Stress (Yield, 23°C)
12000
8410
psi
ISO 527-2
Tensile Strain (Break, 23°C)
5
6
%
ISO 527-2
Flexural Modulus (23°C)
566000
196000
psi
ISO 178
Flexural Strength (23°C)
15500
5660
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
1.62
-
ftlb/in²
-30°C
1.76
-
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
35.7
-
ftlb/in²
-30°C
37.1
-
ftlb/in²
Notched Izod Impact Strength, +23°C
2.85
-
ftlb/in²
ISO 180/1A
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
167
-
°F
0.45 MPa, Unannealed
464
-
°F
Melting Temperature
509
*
°F
ISO 11357-3
RTI Elec
UL 746
0.400 mm
248
°F
0.750 mm
248
°F
1.50 mm
248
°F
3.00 mm
248
°F
RTI Imp
UL 746
0.400 mm
167
°F
0.750 mm
176
°F
1.50mm
176
°F
3.00 mm
176
°F
RTI Str
UL 746
0.400 mm
221
°F
0.750 mm
230
°F
1.50 mm
230
°F
3.00 mm
230
°F
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E8
-
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
432
-
kV/in
IEC 60243
Arc Resistance (3.00 mm)
5
ASTM D 495
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.400 mm
PLC 2
0.750 mm
PLC 1
1.50 mm
PLC 1
3.00 mm
PLC 1
High Voltage Arc Tracking Rate (HVTR), 3.00 mm
PLC 0
UL 746
Hot-wire Ignition (HWI)
UL 746
0.400 mm
PLC 4
0.750 mm
PLC 4
1.50 mm
PLC 3
3.00 mm
PLC 2
Flammability
dry
cond.
Unit
Test Norm
Flammability
UL 94
0.400 mm
V-0
0.750 mm
V-0
1.50 mm
V-0
3.00 mm
V-0
Glow Wire Flammability Index
IEC 60695-2-12
0.400 mm
1760
°F
0.750 mm
1760
°F
1.50 mm
1760
°F
3.00 mm
1760
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
0.400 mm
1760
°F
0.750 mm
1760
°F
1.50 mm
1290
°F
3.00 mm
1290
°F
Oxygen index
35
*
%
EN ISO 4589-2
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Rear Temperature
500 - 554
°F
Middle Temperature
500 - 554
°F
Front Temperature
500 - 554
°F
Nozzle temperature
500 - 554
°F
Processing (Melt) Temperature
518 - 545
°F
Mold Temperature
149 - 203
°F