Starflam AFR450X2 is a 25% glass filled, red phosphorous flame retardant PA66 for injection molded applications.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Flame Retardant, Halogen Content, None
Uses
Flame Retardant
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.38
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.0
*
%
Flow : 23°C, 2.00 mm
0.5
*
%
Water Absorption
ISO 62
23°C, 24 hr
1
*
%
Equilibrium, 23°C, 50% RH
1.7
*
%
Water Absorption, Saturation, 23°C
6
%
ISO 62
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.25E6
812213
psi
ISO 527-2
Tensile Stress (Break, 23°C)
20200
13100
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.6
4.8
%
ISO 527-2
Flexural Modulus (23°C)
1.19E6
740000
psi
ISO 178
Flexural Strength (23°C)
29400
17300
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
5.23
6.66
ftlb/in²
-30°C
3.71
3.66
ftlb/in²
-40°C
3.47
3.33
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
31.9
34.3
ftlb/in²
-30°C
28.5
27.6
ftlb/in²
-40°C
27.6
27.1
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
4.61
6.18
ftlb/in²
-30°C
3.52
3.47
ftlb/in²
-40°C
3.47
3.19
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
462
437
°F
0.45 MPa, Unannealed
496
493
°F
Melting Temperature
502
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
28
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
90
*
E-6/K
RTI Elec
UL 746
0.750 mm
230
°F
1.50 mm
230
°F
3.00 mm
230
°F
RTI Imp
UL 746
0.750 mm
230
°F
1.50mm
230
°F
3.00 mm
230
°F
RTI Str
UL 746
0.750 mm
239
°F
1.50 mm
239
°F
3.00 mm
248
°F
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E13
-
Ohm*m
IEC 60093
Surface resistivity (1.00 mm)
1E16
-
Ohm
IEC 62631-3-2
Dielectric Strength (1.00 mm)
610
559
kV/in
IEC 60243
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.750 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
Hot-wire Ignition (HWI)
UL 746
0.750 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
Flammability
Value
Test Norm
Flammability
UL 94
0.750 mm
V-2
1.50 mm
V-0
3.00 mm
V-0
Injection
Value
Unit
Drying Temperature
167 - 185
°F
Drying Time
4
h
Suggested Max Moisture
0.1
%
Rear Temperature
527 - 545
°F
Middle Temperature
527 - 545
°F
Front Temperature
518 - 545
°F
Processing (Melt) Temperature
527 - 545
°F
Mold Temperature
140 - 194
°F
Applications
Solar Junction Boxes and Connectors
Energy Management/Solar
Residential MCB, MCCB
Power Management
Battery Disconnect Unit Carrier and Cover
Vehicles