Starflam AFR470X2I BK0939 is a 35% glass filled, halogen free, red phosphorus based flame retardant PA66 for injection molding applications.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Lubricant
Features
Flame Retardant, Laser Markable, Lubricated, Organic Heat Stabilized
Uses
Flame Retardant, Glass Reinforced
Agency Rating
ASTM, D4066 PA0120G35 A43370, ASTM, D6779 PA0120G35 A43370, SAE, J1639 PA661116
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.47
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.5
*
%
Flow : 23°C, 2.00 mm
0.1
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.9
*
%
Equilibrium, 23°C, 50% RH
1.2
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.61E6
1.39E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
23200
16000
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.6
3.3
%
ISO 527-2
Flexural Modulus (23°C)
1.45E6
1.23E6
psi
ISO 178
Flexural Strength (23°C)
32600
25100
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
5.71
6.18
ftlb/in²
-30°C
4.28
4.33
ftlb/in²
-40°C
4.28
4.28
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
33.3
33.3
ftlb/in²
-30°C
30.9
29.5
ftlb/in²
-40°C
30.9
30
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
5.71
6.66
ftlb/in²
-30°C
4.28
4.76
ftlb/in²
-40°C
4.04
4.76
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
464
455
°F
0.45 MPa, Unannealed
500
493
°F
Melting Temperature
500
*
°F
ISO 11357-3
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
610
533
kV/in
IEC 60243
Flammability
Value
Unit
Test Norm
Flammability
UL 94
0.750 mm
V-0
1.50 mm
V-0
3.00 mm
V-0
Glow Wire Ignition Temperature
IEC 60695-2-13
0.750 mm
1520
°F
Injection
Value
Unit
Drying Temperature
158 - 176
°F
Drying Time
2 - 4
h
Suggested Max Regrind
25
%
Suggested Max Moisture
0.05
%
Rear Temperature
≤545
°F
Middle Temperature
≤554
°F
Front Temperature
≤554
°F
Nozzle temperature
≤554
°F
Processing (Melt) Temperature
≤572
°F