Product Texts
Starflam RF0023E is a mineral filled, glass fiber reinforced, flame retardant (PA66+PA6)-blend for injection molded applications. The material is halogen free and red phosphorus free.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Flame Retardant, Halogen Content, None
Uses
Flame Retardant, Glass/Mineral Reinforced
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Water Absorption
ISO 62
23°C, 24 hr
0.6
*
%
Equilibrium, 23°C, 50% RH
1.3
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.55E6
797709
psi
ISO 527-2
Tensile Stress (Break, 23°C)
12500
8410
psi
ISO 527-2
Tensile Strain (Break, 23°C)
1.4
2.4
%
ISO 527-2
Flexural Modulus (23°C)
1.61E6
754000
psi
ISO 178
Flexural Strength (23°C)
19900
11700
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
1.71
1.95
ftlb/in²
-30°C
1.66
1.62
ftlb/in²
-40°C
1.66
1.57
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
9.99
16.2
ftlb/in²
-30°C
9.51
8.56
ftlb/in²
-40°C
9.51
8.56
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
1.9
2.05
ftlb/in²
-30°C
1.71
1.62
ftlb/in²
-40°C
1.71
1.57
ftlb/in²
Unnotched Izod Impact Strength, +23°C
10.5
-
ftlb/in²
ISO 180/1U
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
412
387
°F
0.45 MPa, Unannealed
455
441
°F
Melting Temperature
500
*
°F
ISO 11357-3
RTI Elec
UL 746
0.860 mm
266
°F
1.70 mm
266
°F
3.00 mm
266
°F
RTI Imp
UL 746
0.860 mm
221
°F
1.70 mm
221
°F
3.00 mm
221
°F
RTI Str
UL 746
0.860 mm
248
°F
1.70 mm
266
°F
3.00 mm
284
°F
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
635
610
kV/in
IEC 60243
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.860 mm
PLC 0
1.70 mm
PLC 0
3.00 mm
PLC 0
High Voltage Arc Tracking Rate (HVTR), 3.00 mm
PLC 0
UL 746
Hot-wire Ignition (HWI)
UL 746
0.860 mm
PLC 0
Flammability
Value
Test Norm
Flammability
UL 94
0.860 mm
V-2
1.70 mm
V-0
3.00 mm
V-0
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
≤0.2
%
Rear Temperature
518 - 536
°F
Middle Temperature
527 - 545
°F
Front Temperature
536 - 572
°F
Processing (Melt) Temperature
536 - 572
°F
Mold Temperature
140 - 194
°F