Product Texts
Starflam RF0077P is a glass fiber reinforced, flame retardant PA66+PA6 for injection molded applications. The material is halogen free and red phosphorus free.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Flame Retardant, Halogen Content, None
Uses
Flame Retardant
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.49
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.8
*
%
Flow : 23°C, 2.00 mm
0.2
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.9
*
%
Equilibrium, 23°C, 50% RH
0.8
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
2E6
1.49E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
20200
16200
psi
ISO 527-2
Tensile Strain (Break, 23°C)
1.7
2.2
%
ISO 527-2
Flexural Modulus (23°C)
1.68E6
1.36E6
psi
ISO 178
Flexural Strength (23°C)
31200
25700
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
3.95
4.52
ftlb/in²
-30°C
4.09
3.81
ftlb/in²
-40°C
3.81
3.71
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
25.2
29
ftlb/in²
-30°C
24.7
23.8
ftlb/in²
-40°C
22.8
21.9
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
3.43
4.23
ftlb/in²
-30°C
3.38
3.76
ftlb/in²
-40°C
3.71
3.66
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
444
433
°F
0.45 MPa, Unannealed
486
478
°F
Melting Temperature
495
*
°F
ISO 11357-3
RTI Elec
UL 746
0.800 mm
284
°F
1.50 mm
284
°F
3.00 mm
284
°F
RTI Imp
UL 746
0.800 mm
230
°F
1.50mm
230
°F
3.00 mm
230
°F
RTI Str
UL 746
0.800 mm
284
°F
1.50 mm
284
°F
3.00 mm
284
°F
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
762
711
kV/in
IEC 60243
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.800 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
Hot-wire Ignition (HWI)
UL 746
0.800 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
Flammability
Value
Unit
Test Norm
Flammability
UL 94
0.800 mm
V-0
1.50 mm
V-0
3.00 mm
V-0
Glow Wire Flammability Index
IEC 60695-2-12
0.800 mm
1760
°F
1.50 mm
1760
°F
3.00 mm
1760
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
0.800 mm
1430
°F
1.50 mm
1430
°F
3.00 mm
1520
°F
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
509 - 527
°F
Middle Temperature
509 - 527
°F
Front Temperature
509 - 536
°F
Processing (Melt) Temperature
518 - 536
°F
Mold Temperature
140 - 212
°F