Starflam X-Protect RX07034 is a 30% glass fiber reinforced PA66 + PA6 compound. Developed for use in Arc chambers and other injection molding applications, it has low smoke and easy processing.
General
Additive
Heat Stabilizer, Lubricant, Release agent
Features
Flame Retardant, Good Electrical Properties, Lubricated
Uses
Flame Retardant
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.54
-
g/cm³
ISO 1183
Mechanical
dry
cond.
Unit
Test Norm
Tensile Stress (Break, 23°C)
24700
-
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.3
-
%
ISO 527-2
Flexural Modulus (23°C)
1.38E6
-
psi
ISO 178
Flexural Strength (23°C)
32600
-
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
4.28
-
ftlb/in²
ISO 180/1A
Unnotched Izod Impact Strength, +23°C
28.5
-
ftlb/in²
ISO 180/1U
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature, 1.80 MPa, Unannealed
415
-
°F
ISO 75-2/A
RTI Elec
UL 746
0.800 mm
284
°F
1.60 mm
284
°F
RTI Imp
UL 746
0.800 mm
212
°F
1.60 mm
212
°F
RTI Str
UL 746
0.800 mm
284
°F
1.60 mm
284
°F
Electrical
Value
Unit
Test Norm
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.800 mm
PLC 0
1.60 mm
PLC 0
Hot-wire Ignition (HWI)
UL 746
0.800 mm
PLC 2
1.60 mm
PLC 1
Flammability
Value
Unit
Test Norm
Flammability
UL 94
0.800 mm
HB
1.60 mm
HB
Glow Wire Flammability Index
IEC 60695-2-12
1.60 mm
1340
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
1.60 mm
1380
°F
Injection
Value
Unit
Drying Temperature
≤140
°F
Drying Time
≤4
h
Suggested Max Moisture
≤0.2
%
Rear Temperature
500 - 536
°F
Middle Temperature
518 - 536
°F
Front Temperature
482 - 518
°F
Nozzle temperature
518 - 536
°F
Processing (Melt) Temperature
500 - 536
°F
Mold Temperature
104 - 194
°F