Product Texts
Starflam BFR552Y3 is a glass and mineral filled, flame retardant PA6 for injection molded applications. The material is halogen free and red phosphorus free.
General
Additive
Flame Retarding Agent, Release agent
Features
Flame Retardant, Good Dimensional Stability
Uses
Flame Retardant, Glass/Mineral Reinforced
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.34
-
g/cm³
ISO 1183
Water Absorption
ISO 62
Equilibrium, 23°C, 50% RH
1.2
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
841220
-
psi
ISO 527-2
Tensile Stress (Break, 23°C)
12300
-
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.8
-
%
ISO 527-2
Flexural Modulus (23°C)
798000
-
psi
ISO 178
Flexural Strength (23°C)
21000
-
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
1.43
-
ftlb/in²
-30°C
0.951
-
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
14.3
-
ftlb/in²
-30°C
11.9
-
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
1.9
-
ftlb/in²
-40°C
1.43
-
ftlb/in²
Thermal
Value
Unit
Test Norm
RTI Elec
UL 746
0.750 mm
149
°F
3.00 mm
149
°F
RTI Imp
UL 746
0.750 mm
149
°F
3.00 mm
149
°F
RTI Str
UL 746
0.750 mm
149
°F
3.00 mm
149
°F
Electrical
Value
Test Norm
High Amp Arc Ignition (HAI)
UL 746
0.750 mm
PLC 0
3.00 mm
PLC 0
Hot-wire Ignition (HWI)
UL 746
0.750 mm
PLC 3
Flammability
Value
Test Norm
Flammability
UL 94
0.750 mm
V-2
3.00 mm
V-2
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
464 - 482
°F
Middle Temperature
482 - 500
°F
Front Temperature
482 - 518
°F
Processing (Melt) Temperature
482 - 518
°F
Mold Temperature
122 - 194
°F