Starflam PA6Z22V2D is an unfilled flame retardant PA6 resin for injection molded applications. The material is halogen free and red phosphorus free.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Bromine Free, Flame Retardant, Halogen Content, None
Uses
Flame Retardant
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.18
-
g/cm³
ISO 1183
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
493129
-
psi
ISO 527-2
Tensile Stress (Break, 23°C)
10300
-
psi
ISO 527-2
Tensile Strain (Break, 23°C)
10
-
%
ISO 527-2
Flexural Modulus (23°C)
377000
-
psi
ISO 178
Flexural Strength (23°C)
13200
-
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength, +23°C
2.47
-
ftlb/in²
ISO 179/1eA
Charpy Unnotched Impact Strength, +23°C
46.1
-
ftlb/in²
ISO 179/1eU
Notched Izod Impact Strength, +23°C
3.04
-
ftlb/in²
ISO 180/1A
Unnotched Izod Impact Strength, +23°C
51.4
-
ftlb/in²
ISO 180/1U
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature, 1.80 MPa, Unannealed
127
-
°F
ISO 75-2/A
Melting Temperature
430
*
°F
ISO 11357-3
Flammability
Value
Unit
Test Norm
Glow Wire Flammability Index
IEC 60695-2-12
1.60 mm
1760
°F
Injection
Value
Unit
Drying Temperature
167 - 185
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
446 - 464
°F
Middle Temperature
455 - 473
°F
Front Temperature
464 - 500
°F
Processing (Melt) Temperature
464 - 500
°F
Mold Temperature
140 - 176
°F