Product Texts
Starflam PK0022E is a mineral filled, flame retardant PA6 for injection molded applications. The material is halogen free and red phosphorus free.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Flame Retardant, Halogen Content, None
Uses
Flame Retardant, Mineral Reinforced
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.24
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.3
*
%
Flow : 23°C, 2.00 mm
1.3
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.3
*
%
Equilibrium, 23°C, 50% RH
2
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
623663
261068
psi
ISO 527-2
Tensile Stress (Break, 23°C)
11200
5660
psi
ISO 527-2
Tensile Strain (Break, 23°C)
5.4
12
%
ISO 527-2
Flexural Modulus (23°C)
609000
174000
psi
ISO 178
Flexural Strength (23°C)
15200
3920
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
2.14
3
ftlb/in²
-30°C
1.9
1.95
ftlb/in²
-40°C
1.9
1.66
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
29
32.3
ftlb/in²
-30°C
31.4
32.3
ftlb/in²
-40°C
32.8
30.9
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
1.86
2.81
ftlb/in²
-30°C
1.9
2.05
ftlb/in²
-40°C
1.95
2.24
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
172
199
°F
0.45 MPa, Unannealed
388
360
°F
Melting Temperature
430
*
°F
ISO 11357-3
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
762
584
kV/in
IEC 60243
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
464 - 482
°F
Middle Temperature
482 - 500
°F
Front Temperature
482 - 518
°F
Processing (Melt) Temperature
482 - 518
°F
Mold Temperature
122 - 194
°F