Product Texts
Starflam PK0052E is a 25% mineral filled, flame retardant PA6 for injection molded applications. The material is halogen free and red phosphorus free.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Flame Retardant, Halogen Content, None
Uses
Flame Retardant, Mineral Reinforced
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.38
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.9
*
%
Flow : 23°C, 2.00 mm
0.9
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.9
*
%
Equilibrium, 23°C, 50% RH
1.4
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
899236
536641
psi
ISO 527-2
Tensile Stress (Break, 23°C)
10000
5660
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3
4
%
ISO 527-2
Flexural Modulus (23°C)
1000000
363000
psi
ISO 178
Flexural Strength (23°C)
17300
6380
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
1.52
2.24
ftlb/in²
-30°C
1.33
1.19
ftlb/in²
-40°C
1.62
1.05
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
15.2
19.5
ftlb/in²
-30°C
15.2
17.6
ftlb/in²
-40°C
16.6
15.7
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
1.43
1.57
ftlb/in²
-30°C
1.62
1.33
ftlb/in²
-40°C
1.33
1.05
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
246
232
°F
0.45 MPa, Unannealed
394
379
°F
Melting Temperature
430
*
°F
ISO 11357-3
RTI Elec
UL 746
0.800 mm
149
°F
RTI Imp
UL 746
0.800 mm
149
°F
RTI Str
UL 746
0.800 mm
149
°F
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E13
-
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
737
737
kV/in
IEC 60243
Flammability
Value
Test Norm
Flammability
UL 94
0.800 mm
V-2
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
464 - 482
°F
Middle Temperature
482 - 500
°F
Front Temperature
482 - 518
°F
Processing (Melt) Temperature
482 - 518
°F
Mold Temperature
122 - 194
°F