Product Texts
Starflam PK0069 is a mineral filled, flame retardant, PA6, for injection molded applications.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Flame Retardant, Halogenated
Uses
Flame Retardant, Mineral Reinforced
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.66
-
g/cm³
ISO 1183
Water Absorption, 23°C, 24 hr
0.8
*
%
ISO 62
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
899236
-
psi
ISO 527-2
Tensile Stress (Break, 23°C)
9140
-
psi
ISO 527-2
Tensile Strain (Break, 23°C)
1.5
-
%
ISO 527-2
Flexural Modulus (23°C)
1.07E6
-
psi
ISO 178
Flexural Strength (23°C)
14600
-
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
2.38
-
ftlb/in²
ISO 180/1A
Unnotched Izod Impact Strength, +23°C
7.14
-
ftlb/in²
ISO 180/1U
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
266
-
°F
0.45 MPa, Unannealed
379
-
°F
RTI Elec
UL 746
1.50 mm
149
°F
RTI Imp
UL 746
1.50mm
149
°F
RTI Str
UL 746
1.50 mm
149
°F
Flammability
Value
Test Norm
Flammability
UL 94
1.50 mm
V-0
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
464 - 482
°F
Middle Temperature
482 - 500
°F
Front Temperature
482 - 518
°F
Processing (Melt) Temperature
482 - 518
°F
Mold Temperature
122 - 194
°F