Starflam PW0042E is a mineral filled, flame retardant PA6 for injection molded applications. The material is halogen free and red phosphorus free.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Flame Retardant, Halogen Content, None
Uses
Flame Retardant, Mineral Reinforced
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.34
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.0
*
%
Flow : 23°C, 2.00 mm
1.1
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.4
*
%
Equilibrium, 23°C, 50% RH
1.7
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
754198
319084
psi
ISO 527-2
Tensile Stress (Break, 23°C)
10600
4790
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.8
12
%
ISO 527-2
Flexural Modulus (23°C)
754000
305000
psi
ISO 178
Flexural Strength (23°C)
15800
5800
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
1.47
1.95
ftlb/in²
-30°C
1.24
1.05
ftlb/in²
-40°C
1.24
0.999
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
18.1
36.2
ftlb/in²
-30°C
17.1
14.7
ftlb/in²
-40°C
14.7
14.3
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
1.86
2.33
ftlb/in²
-30°C
1.62
1.28
ftlb/in²
-40°C
1.47
1.28
ftlb/in²
Unnotched Izod Impact Strength, +23°C
21.4
-
ftlb/in²
ISO 180/1U
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
183
-
°F
0.45 MPa, Unannealed
370
-
°F
Melting Temperature
428
*
°F
ISO 11357-3
RTI Elec
UL 746
0.750 mm
149
°F
RTI Imp
UL 746
0.750 mm
149
°F
RTI Str
UL 746
0.750 mm
149
°F
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
635
533
kV/in
IEC 60243
Flammability
Value
Test Norm
Flammability
UL 94
0.750 mm
V-2
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
464 - 482
°F
Middle Temperature
482 - 500
°F
Front Temperature
482 - 518
°F
Processing (Melt) Temperature
482 - 518
°F
Mold Temperature
122 - 194
°F