Starflam PX06010 is a 25% glass filled, flame retardant PA6 for injection molded applications. The material is halogen free and red phosphorus free.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Flame Retardant
Uses
Flame Retardant
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.37
-
g/cm³
ISO 1183
Water Absorption, 23°C, 24 hr
1.9
*
%
ISO 62
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
913739
-
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
12200
-
psi
ISO 527-2
Tensile Stress (Break, 23°C)
11700
-
psi
ISO 527-2
Tensile Strain (Yield, 23°C)
2.3
-
%
ISO 527-2
Flexural Modulus (23°C)
798000
-
psi
ISO 178
Flexural Strength (23°C)
19900
-
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Notched Izod Impact Strength, +23°C
2.38
-
ftlb/in²
ISO 180/1A
Unnotched Izod Impact Strength, +23°C
16.6
-
ftlb/in²
ISO 180/1U
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
316
-
°F
0.45 MPa, Unannealed
403
-
°F
RTI Elec
UL 746
0.750 mm
257
°F
1.50 mm
257
°F
3.00 mm
257
°F
RTI Imp
UL 746
0.750 mm
257
°F
1.50mm
257
°F
3.00 mm
257
°F
RTI Str
UL 746
0.750 mm
266
°F
1.50 mm
266
°F
3.00 mm
284
°F
Electrical
Value
Unit
Test Norm
Comparative Tracking Index (3.00 mm)
400 - 599
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.750 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
Hot-wire Ignition (HWI)
UL 746
0.750 mm
PLC 2
1.50 mm
PLC 2
3.00 mm
PLC 2
Flammability
Value
Test Norm
Flammability
UL 94
0.750 mm
V-2
1.50 mm
V-2
3.00 mm
V-2
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
464 - 482
°F
Middle Temperature
482 - 500
°F
Front Temperature
482 - 518
°F
Processing (Melt) Temperature
482 - 518
°F
Mold Temperature
122 - 194
°F