Product Texts
Starflam PX06020 is an unfilled, halogen free and red phosphorous free, flame retardant, PA6 for injection molded applications.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Bromine Free, Flame Retardant, Halogen Content, None
Uses
Flame Retardant
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.16
-
g/cm³
ISO 1183
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
493129
-
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
11300
-
psi
ISO 527-2
Tensile Strain (Yield, 23°C)
3.7
-
%
ISO 527-2
Tensile Strain (Break, 23°C)
5.6
-
%
ISO 527-2
Flexural Modulus (23°C)
450000
-
psi
ISO 178
Flexural Strength (23°C)
15200
-
psi
ISO 178
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
167
-
°F
0.45 MPa, Unannealed
374
-
°F
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
75
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
80
*
E-6/K
RTI Elec
UL 746
0.750 mm
248
°F
1.50 mm
248
°F
3.00 mm
248
°F
RTI Imp
UL 746
0.750 mm
149
°F
1.50mm
167
°F
3.00 mm
167
°F
RTI Str
UL 746
0.750 mm
185
°F
1.50 mm
185
°F
3.00 mm
185
°F
Electrical
Value
Unit
Test Norm
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.750 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
Hot-wire Ignition (HWI)
UL 746
0.750 mm
PLC 4
Flammability
dry
cond.
Unit
Test Norm
Flammability
UL 94
0.400 mm
V-0
0.750 mm
V-0
1.50 mm
V-0
3.00 mm
V-0
Glow Wire Flammability Index
IEC 60695-2-12
0.750 mm
1760
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
0.750 mm
1340
°F
Oxygen index
32
*
%
EN ISO 4589-2
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
464 - 482
°F
Middle Temperature
482 - 500
°F
Front Temperature
482 - 518
°F
Processing (Melt) Temperature
482 - 518
°F
Mold Temperature
122 - 194
°F