Starflam PZ0042E is a 20% glass filled, flame retardant PA6 for injection molded applications. The material is halogen free and red phosphorus free.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Flame Retardant, Halogen Content, None
Uses
Flame Retardant
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.31
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.9
*
%
Flow : 23°C, 2.00 mm
0.7
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.7
*
%
Equilibrium, 23°C, 50% RH
1.8
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
855724
406106
psi
ISO 527-2
Tensile Stress (Break, 23°C)
12600
6530
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3.2
11
%
ISO 527-2
Flexural Modulus (23°C)
841000
363000
psi
ISO 178
Flexural Strength (23°C)
19700
7540
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
1.81
4.66
ftlb/in²
-30°C
1.86
2
ftlb/in²
-40°C
1.71
1.86
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
15.7
37.1
ftlb/in²
-30°C
15.2
19
ftlb/in²
-40°C
16.6
22.8
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
1.9
4.33
ftlb/in²
-30°C
1.86
2.24
ftlb/in²
-40°C
2.14
1.76
ftlb/in²
Unnotched Izod Impact Strength, +23°C
21.4
-
ftlb/in²
ISO 180/1U
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
378
336
°F
0.45 MPa, Unannealed
419
401
°F
Melting Temperature
432
*
°F
ISO 11357-3
RTI Elec
UL 746
0.750 mm
257
°F
0.800 mm
257
°F
1.00 mm
257
°F
1.50 mm
257
°F
3.00 mm
257
°F
RTI Imp
UL 746
0.750 mm
257
°F
0.800 mm
257
°F
1.00 mm
257
°F
1.50mm
257
°F
3.00 mm
257
°F
RTI Str
UL 746
0.750 mm
266
°F
0.800 mm
266
°F
1.00 mm
266
°F
1.50 mm
266
°F
3.00 mm
266
°F
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
686
660
kV/in
IEC 60243
High Amp Arc Ignition (HAI)
UL 746
0.750 mm
PLC 3
0.800 mm
PLC 0
1.00 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
Hot-wire Ignition (HWI)
UL 746
0.750 mm
PLC 0
0.800 mm
PLC 0
1.00 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
Flammability
Value
Unit
Test Norm
Flammability
UL 94
0.750 mm
V-2
0.800 mm
V-2
1.50 mm
V-2
3.00 mm
V-2
Glow Wire Flammability Index
IEC 60695-2-12
1.00 mm
1760
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
1.00 mm
1340
°F
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
464 - 482
°F
Middle Temperature
482 - 500
°F
Front Temperature
482 - 518
°F
Processing (Melt) Temperature
482 - 518
°F
Mold Temperature
122 - 194
°F