Starflam 315J BK0707 (formerly Vydyne® ECO315J BK0707) is a non-halogenated, unfilled, flame-retardant PA66/6 copolymer with excellent toughness and ductility. 315J BK0707 is also lubricated for machine feed and easy mold release.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Lubricant
Features
Crack Resistant, Ductile, Flame Retardant, Good Mold Release, Good Toughness, Halogen Content, None, High Elongation, Low Density, Lubricated, Organic Heat Stabilized
Uses
Flame Retardant
UL File Number
E70062
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.16
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.4
*
%
Flow : 23°C, 2.00 mm
1.2
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.8
*
%
Equilibrium, 23°C, 50% RH
2.3
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
471374
174046
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
10900
6090
psi
ISO 527-2
Tensile Strain (Yield, 23°C)
3.5
23
%
ISO 527-2
Tensile Strain (Break, 23°C)
22
140
%
ISO 527-2
Flexural Modulus (23°C)
464000
226000
psi
ISO 178
Flexural Strength (23°C)
13300
6530
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
2.57
-
ftlb/in²
-30°C
2.57
-
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
N
-
ftlb/in²
-30°C
N
-
ftlb/in²
Notched Izod Impact Strength, +23°C
2.85
-
ftlb/in²
ISO 180/1A
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
149
-
°F
0.45 MPa, Unannealed
437
-
°F
Melting Temperature
471
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
110
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
110
*
E-6/K
RTI Elec
UL 746
0.400 mm
266
°F
0.750 mm
266
°F
1.50 mm
266
°F
3.00 mm
266
°F
RTI Imp
UL 746
0.400 mm
149
°F
0.750 mm
149
°F
1.50mm
185
°F
3.00 mm
185
°F
RTI Str
UL 746
0.400 mm
212
°F
0.750 mm
212
°F
1.50 mm
212
°F
3.00 mm
230
°F
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E9
-
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
330
-
kV/in
IEC 60243
Arc Resistance (3.00 mm)
5
ASTM D 495
Comparative Tracking Index (3.00 mm)
600
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.400 mm
PLC 0
0.750 mm
PLC 0
1.50 mm
PLC 0
3.00 mm
PLC 0
High Voltage Arc Tracking Rate (HVTR), 3.00 mm
PLC 1
UL 746
Hot-wire Ignition (HWI)
UL 746
0.400 mm
PLC 4
0.750 mm
PLC 4
1.50 mm
PLC 4
3.00 mm
PLC 3
Flammability
dry
cond.
Unit
Test Norm
Flammability
UL 94
0.400 mm
V-0
0.750 mm
V-0
1.50 mm
V-0
3.00 mm
V-0
Glow Wire Flammability Index
IEC 60695-2-12
0.400 mm
1760
°F
0.750 mm
1760
°F
1.50 mm
1760
°F
3.00 mm
1760
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
0.400 mm
1610
°F
0.750 mm
1610
°F
1.50 mm
1430
°F
3.00 mm
1340
°F
Oxygen index
29
*
%
EN ISO 4589-2
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Suggested Max Regrind
50
%
Rear Temperature
464 - 518
°F
Middle Temperature
464 - 518
°F
Front Temperature
464 - 518
°F
Nozzle temperature
464 - 518
°F
Processing (Melt) Temperature
482 - 518
°F
Mold Temperature
149 - 203
°F