Starflam 909 (formerly Vydyne® 909) is a halogenated, 25% glass-filled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and easy mold release.
General
Additive
Flame Retarding Agent, Lubricant
Features
Crack Resistant, Flame Retardant, Good Mold Release, Good Toughness, Halogenated, High Rigidity, High Strength, Ignition Resistant, Lubricated
Uses
Flame Retardant
UL File Number
E70062
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.47
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.0
*
%
Flow : 23°C, 2.00 mm
0.4
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.7
*
%
Equilibrium, 23°C, 50% RH
1.3
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.32E6
1.03E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
19100
13100
psi
ISO 527-2
Tensile Strain (Break, 23°C)
2.2
3
%
ISO 527-2
Flexural Modulus (23°C)
1.2E6
725000
psi
ISO 178
Flexural Strength (23°C)
28000
20300
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
4.47
-
ftlb/in²
-30°C
4.52
-
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
19
-
ftlb/in²
-30°C
16.6
-
ftlb/in²
Notched Izod Impact Strength, +23°C
4.28
-
ftlb/in²
ISO 180/1A
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
446
-
°F
0.45 MPa, Unannealed
482
-
°F
Melting Temperature
482
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
20
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
100
*
E-6/K
RTI Elec
UL 746
0.750 mm
266
°F
1.50 mm
266
°F
3.00 mm
266
°F
RTI Imp
UL 746
0.750 mm
149
°F
1.50mm
203
°F
3.00 mm
203
°F
RTI Str
UL 746
0.750 mm
230
°F
1.50 mm
230
°F
3.00 mm
230
°F
Electrical
Value
Test Norm
Arc Resistance (3.00 mm)
6
ASTM D 495
High Amp Arc Ignition (HAI)
UL 746
0.750 mm
PLC 0
1.50 mm
PLC 0
High Voltage Arc Tracking Rate (HVTR), 3.00 mm
PLC 3
UL 746
Hot-wire Ignition (HWI)
UL 746
0.750 mm
PLC 0
1.50 mm
PLC 0
Flammability
Value
Unit
Test Norm
Flammability
UL 94
0.400 mm
V-0
0.750 mm
V-0
1.50 mm
V-0
3.00 mm
V-0
Flammability, 5V
UL 94
1.50 mm
5VA
3.00 mm
5VA
Glow Wire Flammability Index
IEC 60695-2-12
0.400 mm
1760
°F
0.750 mm
1760
°F
1.50 mm
1760
°F
3.00 mm
1760
°F
Glow Wire Ignition Temperature
IEC 60695-2-13
0.400 mm
1710
°F
0.750 mm
1380
°F
1.50 mm
1380
°F
3.00 mm
1470
°F
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Rear Temperature
464 - 518
°F
Middle Temperature
464 - 518
°F
Front Temperature
464 - 518
°F
Nozzle temperature
464 - 518
°F
Processing (Melt) Temperature
482 - 518
°F
Mold Temperature
149 - 203
°F