Starflam R10002E is a flame retardant PA66/6 for injection molded applications. The material is halogen free and red phosphorus free.
General
Additive
Flame Retarding Agent, Heat Stabilizer, Release agent
Features
Bromine Free, Flame Retardant, Halogen Content, None
Uses
Flame Retardant
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.18
-
g/cm³
ISO 1183
Water Absorption
ISO 62
23°C, 24 hr
1.6
*
%
Equilibrium, 23°C, 50% RH
1.8
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
594656
333587
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
11900
6960
psi
ISO 527-2
Tensile Strain (Break, 23°C)
4.9
6.2
%
ISO 527-2
Flexural Modulus (23°C)
522000
218000
psi
ISO 178
Flexural Strength (23°C)
14800
5370
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
1.71
2.19
ftlb/in²
-30°C
1.19
1.24
ftlb/in²
-40°C
1.47
0.904
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
26.2
32.3
ftlb/in²
-30°C
24.7
11.4
ftlb/in²
-40°C
22.8
N
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
1.86
1.71
ftlb/in²
-30°C
1.71
1.52
ftlb/in²
-40°C
1.71
1.24
ftlb/in²
Unnotched Izod Impact Strength, +23°C
28.5
-
ftlb/in²
ISO 180/1U
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
165
-
°F
0.45 MPa, Unannealed
372
372
°F
Melting Temperature
504
*
°F
ISO 11357-3
RTI Elec
UL 746
0.400 mm
149
°F
0.800 mm
248
°F
1.60 mm
248
°F
3.00 mm
248
°F
RTI Imp
UL 746
0.400 mm
149
°F
0.800 mm
149
°F
1.60 mm
167
°F
3.00 mm
167
°F
RTI Str
UL 746
0.400 mm
149
°F
0.800 mm
185
°F
1.60 mm
185
°F
3.00 mm
185
°F
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
660
508
kV/in
IEC 60243
High Amp Arc Ignition (HAI)
UL 746
0.800 mm
PLC 0
Hot-wire Ignition (HWI)
UL 746
0.800 mm
PLC 3
Flammability
Value
Test Norm
Flammability
UL 94
0.400 mm
V-0
0.800 mm
V-0
1.60 mm
V-0
3.00 mm
V-0
Injection
Value
Unit
Drying Temperature
167 - 185
°F
Drying Time
4
h
Suggested Max Moisture
0.2
%
Rear Temperature
500 - 518
°F
Middle Temperature
509 - 536
°F
Front Temperature
518 - 536
°F
Processing (Melt) Temperature
509 - 536
°F
Mold Temperature
140 - 194
°F