Product Texts
HiDura S3MG30H BK0835 is a 30% glass fiber reinforced, heat stabilized polyamide 610 with 42% bio-based content for injection molding applications.
General
Additive
Heat Stabilizer
Features
Chemical Resistant, Oil Resistant, Solvent Resistant
Agency Rating
ASTM, D4066 PA0720A4306, ASTM, D6779 PA0000A4356
Automotive Specifications
Stellantis 01378_22_01243
Appearance
Black
Forms
Pellets
Physical
dry
cond.
Unit
Test Norm
Density
1.31
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.6
*
%
Flow : 23°C, 2.00 mm
0.3
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.4
*
%
Equilibrium, 23°C, 50% RH
1
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.32E6
986258
psi
ISO 527-2
Tensile Stress (Break, 23°C)
22900
17400
psi
ISO 527-2
Tensile Strain (Break, 23°C)
4.4
7.6
%
ISO 527-2
Flexural Modulus (23°C)
1.22E6
899000
psi
ISO 178
Flexural Strength (23°C)
31200
22000
psi
ISO 178
Poisson's Ratio (23°C)
0.38
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
8.56
9.51
ftlb/in²
-30°C
6.18
6.18
ftlb/in²
-40°C
5.23
5.71
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
46.1
48.5
ftlb/in²
-30°C
46.1
41.4
ftlb/in²
-40°C
45.7
41.4
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
7.61
8.56
ftlb/in²
-30°C
6.18
6.18
ftlb/in²
-40°C
5.71
5.71
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
387
379
°F
0.45 MPa, Unannealed
426
421
°F
Melting Temperature
437
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
21
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
120
*
E-6/K
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
813
737
kV/in
IEC 60243
Injection
Value
Unit
Drying Temperature
≥176
°F
Drying Time
≥4
h
Rear Temperature
473 - 527
°F
Middle Temperature
509 - 554
°F
Front Temperature
518 - 572
°F
Nozzle temperature
527 - 581
°F
Processing (Melt) Temperature
491 - 572
°F
Mold Temperature
158 - 212
°F
Applications
Fuel Rail
Powertrain