Product Texts
HiDura S3X NT is a viscosity PA610 grade with 62% bio-based content. It is suitable for monofilament, film, and general purpose injection molding applications; it can also be used for molded applications where high abrasion resistance and ductility are key requirements. PA610 offers a unique balance of thermal, mechanical, and physical properties.
General
Features
Abrasion Resistance, Chemical Resistant, High Viscosity
Agency Rating
ASTM, D4066 PA0710B4301, ASTM, D6779 PA0000B4331
Appearance
Natural Color
Forms
Pellets
Processing Method
Casting, Film Extrusion, Injection Molding, Other Extrusion, Profile Extrusion, Sheet Extrusion
Physical
dry
cond.
Unit
Test Norm
Density
1.07
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.6
*
%
Flow : 23°C, 2.00 mm
1.8
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.5
*
%
Equilibrium, 23°C, 50% RH
1.5
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
275572
159542
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
10400
9860
psi
ISO 527-2
Tensile Stress (Break, 23°C)
10400
9430
psi
ISO 527-2
Tensile Strain (Yield, 23°C)
5.2
21
%
ISO 527-2
Tensile Strain (Break, 23°C)
>50
>50
%
ISO 527-2
Flexural Modulus (23°C)
276000
160000
psi
ISO 178
Flexural Strength (23°C)
8410
4350
psi
ISO 178
Poisson's Ratio (23°C)
0.38
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
3.33
5.71
ftlb/in²
-30°C
3.52
3.81
ftlb/in²
-40°C
3.95
3.66
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
N
N
ftlb/in²
-30°C
N
N
ftlb/in²
-40°C
N
N
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
2.38
4.42
ftlb/in²
-30°C
2.71
3.23
ftlb/in²
-40°C
2.76
3.04
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
126
-
°F
0.45 MPa, Unannealed
250
-
°F
Melting Temperature
437
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
100
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
105
*
E-6/K
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
762
711
kV/in
IEC 60243
Injection
Value
Unit
Drying Temperature
167 - 185
°F
Drying Time
4 - 8
h
Suggested Max Regrind
20
%
Suggested Max Moisture
≤0.2
%
Rear Temperature
518 - 545
°F
Middle Temperature
527 - 554
°F
Front Temperature
527 - 572
°F
Nozzle temperature
527 - 572
°F
Processing (Melt) Temperature
527 - 572
°F
Mold Temperature
149 - 212
°F
Extrusion
Value
Unit
Cylinder Zone 1 Temp
482 - 518
°F
Cylinder Zone 2 Temp
482 - 518
°F
Cylinder Zone 3 Temp
482 - 518
°F
Cylinder Zone 4 Temp
482 - 518
°F
Cylinder Zone 5 Temp
482 - 518
°F
Melt temperature
464 - 509
°F
Die temperature
482 - 518
°F