Product Texts
HiDura D1MG33J NT0864 is an organically heat stabilized, 33% glass filled PA612 designed for injection molding applications.
General
Additive
Heat Stabilizer, Lubricant
Features
Chemical Resistant, Good Colorability, Lubricated, Medium-High Viscosity, Organic Heat Stabilized
Uses
Glass/Mineral Reinforced
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.32
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.7
*
%
Flow : 23°C, 2.00 mm
0.3
*
%
Water Absorption
ISO 62
23°C, 24 hr
0.3
*
%
Equilibrium, 23°C, 50% RH
0.8
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
1.39E6
1.25E6
psi
ISO 527-2
Tensile Stress (Break, 23°C)
24800
20600
psi
ISO 527-2
Tensile Strain (Break, 23°C)
4.3
5.3
%
ISO 527-2
Flexural Modulus (23°C)
1.39E6
1.22E6
psi
ISO 178
Flexural Strength (23°C)
35500
28700
psi
ISO 178
Poisson's Ratio (23°C)
0.39
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
7.14
8.09
ftlb/in²
-30°C
5.71
6.18
ftlb/in²
-40°C
5.71
5.71
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
45.7
44.2
ftlb/in²
-30°C
43.3
42.8
ftlb/in²
-40°C
38.5
39
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
7.61
8.09
ftlb/in²
-30°C
6.18
6.18
ftlb/in²
-40°C
6.18
5.71
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
388
381
°F
0.45 MPa, Unannealed
417
414
°F
Melting Temperature
424
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
20
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
113
*
E-6/K
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
864
838
kV/in
IEC 60243
Injection
Value
Unit
Drying Temperature
176 - 212
°F
Drying Time
4 - 6
h
Suggested Max Regrind
30
%
Suggested Max Moisture
0.15
%
Processing (Melt) Temperature
455 - 554
°F
Mold Temperature
122 - 194
°F