Product Texts
ReDefyne IAI2H BK0858 is a 100% pre-consumer recycled polymer, medium impact modified, heat stabilized PA66. This product balances strength, ductility and thermal resistance making it an excellent choice for automotive fastener applications.
General
Additive
Heat Stabilizer
Features
Abrasion Resistance, Chemical Resistant, Gasoline Resistant, General Purpose, Good Processability, Good Toughness, Heat Stabilized, High Impact Resistance, Impact Modified, Low Temperature Impact Resistance, Low Temperature Toughness, Oil Resistant, Solvent Resistant
Uses
Impact Modified
Automotive Specifications
Ford WRS-M4D706-B2, Renault UB15b, Stellantis MS-DB-41 CPN 1826
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.10
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.6
*
%
Flow : 23°C, 2.00 mm
1.8
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.2
*
%
Equilibrium, 23°C, 50% RH
2.3
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
406106
246565
psi
ISO 527-2
Tensile Stress (Yield, 23°C)
8700
6530
psi
ISO 527-2
Tensile Stress (Break, 23°C)
7540
5800
psi
ISO 527-2
Tensile Strain (Break, 23°C)
22
60
%
ISO 527-2
Flexural Modulus (23°C)
334000
116000
psi
ISO 178
Flexural Strength (23°C)
10200
3480
psi
ISO 178
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
7.61
29.5
ftlb/in²
-30°C
5.23
11.4
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
N
N
ftlb/in²
-30°C
N
N
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
8.56
20.9
ftlb/in²
-30°C
7.61
11.4
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
145
-
°F
0.45 MPa, Unannealed
365
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
111
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
136
*
E-6/K
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E9
-
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
305
-
kV/in
IEC 60243
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Rear Temperature
536 - 590
°F
Middle Temperature
536 - 590
°F
Front Temperature
536 - 590
°F
Nozzle temperature
536 - 590
°F
Processing (Melt) Temperature
545 - 581
°F
Mold Temperature
149 - 203
°F