Product Texts
Vydyne R413H NT is general-purpose, heat-stabilized, impact-modified, 15% glass-fiber reinforced PA66 resin. It is specifically designed to maximize toughness, while retaining physical properties. This product is also lubricated for improved flow and offers superior surface appearance.
General
Additive
Heat Stabilizer, Lubricant
Features
Chemical Resistant, Creep Resistant, Gasoline Resistant, Good Dimensional Stability, Good Flow, Good Impact Strength, Good Mold Release, Grease Resistant, High Rigidity, High Strength, High Tensile Strength, Impact Modified, Lubricated, Oil Resistant, Solvent Resistant
Uses
Glass Reinforced, Impact Modified
Agency Rating
ASTM, D4066 PA016G15, ASTM, D6779 PA016G15
Automotive Specifications
Aptiv M2279V, Stellantis MS-DB-41 CPN 3155, Tesla TM-1006 v3 - 102110 - compliance, Tesla TM-1006 v3 - 202110 - compliance
UL File Number
E70062
Appearance
Natural Color
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.21
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
0.8
*
%
Flow : 23°C, 2.00 mm
0.7
*
%
Water Absorption
ISO 62
23°C, 24 hr
1
*
%
Equilibrium, 23°C, 50% RH
1.9
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
797709
594656
psi
ISO 527-2
Tensile Stress (Break, 23°C)
16000
11600
psi
ISO 527-2
Tensile Strain (Break, 23°C)
5
13
%
ISO 527-2
Flexural Modulus (23°C)
696000
406000
psi
ISO 178
Flexural Strength (23°C)
20300
10600
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
5.71
8.56
ftlb/in²
-30°C
2.85
4.76
ftlb/in²
-40°C
2.38
2.38
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
38.1
36.2
ftlb/in²
-30°C
35.7
33.3
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
5.71
9.99
ftlb/in²
-30°C
4.76
4.76
ftlb/in²
-40°C
4.28
4.28
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
455
-
°F
0.45 MPa, Unannealed
496
-
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
30
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
112
*
E-6/K
Electrical
dry
cond.
Unit
Test Norm
Volume Resistivity (1.00 mm)
1E7
-
Ohm*m
IEC 60093
Dielectric Strength (1.00 mm)
76.2
-
kV/in
IEC 60243
Arc Resistance (3.00 mm)
6
ASTM D 495
Comparative Tracking Index (3.00 mm)
400 - 599
V
IEC 60112
High Amp Arc Ignition (HAI)
UL 746
0.400 mm
PLC 1
0.750 mm
PLC 1
1.50 mm
PLC 1
3.00 mm
PLC 1
High Voltage Arc Tracking Rate (HVTR), 3.00 mm
PLC 3
UL 746
Hot-wire Ignition (HWI)
UL 746
0.400 mm
PLC 4
0.750 mm
PLC 4
1.50 mm
PLC 4
3.00 mm
PLC 4
Flammability
Value
Test Norm
Flammability
UL 94
0.750 mm
HB
1.50 mm
HB
3.00 mm
HB
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Rear Temperature
536 - 590
°F
Middle Temperature
536 - 590
°F
Front Temperature
536 - 590
°F
Nozzle temperature
536 - 590
°F
Processing (Melt) Temperature
545 - 581
°F
Mold Temperature
149 - 203
°F