Product Texts
Vydyne R413J BK0836 is a black, electrically neutral heat stabilized impact-modified, 15% glass-fiber reinforced PA66 resin. R413J BK0836 is designed to produce a light on dark mark using an IR 1064nm laser.
General
Additive
Heat Stabilizer, Release agent
Features
Balanced Stiffness/Toughness, Impact Modified, Laser Markable
Uses
Glass Reinforced, Impact Modified
Agency Rating
ASTM, D4066 PA016G15, ASTM, D6779 PA016G15, SAE, J1639 PA1122
Appearance
Black
Forms
Pellets
Processing Method
Injection Molding
Physical
dry
cond.
Unit
Test Norm
Density
1.21
-
g/cm³
ISO 1183
Molding Shrinkage
ISO 294-4
Across Flow : 23°C, 2.00 mm
1.0
*
%
Flow : 23°C, 2.00 mm
0.8
*
%
Water Absorption
ISO 62
23°C, 24 hr
1.2
*
%
Equilibrium, 23°C, 50% RH
1.9
*
%
Mechanical
dry
cond.
Unit
Test Norm
Tensile Modulus (23°C)
754198
493129
psi
ISO 527-2
Tensile Stress (Break, 23°C)
15100
9570
psi
ISO 527-2
Tensile Strain (Break, 23°C)
3.9
9.4
%
ISO 527-2
Flexural Modulus (23°C)
711000
435000
psi
ISO 178
Flexural Strength (23°C)
18900
11500
psi
ISO 178
Poisson's Ratio (23°C)
0.4
ISO 527-2
Impact
dry
cond.
Unit
Test Norm
Charpy Notched Impact Strength
ISO 179/1eA
+23°C
5.71
5.23
ftlb/in²
-30°C
2.43
3
ftlb/in²
-40°C
2.28
2.9
ftlb/in²
Charpy Unnotched Impact Strength
ISO 179/1eU
+23°C
31.9
40.4
ftlb/in²
-30°C
30.9
32.3
ftlb/in²
-40°C
29
28.5
ftlb/in²
Notched Izod Impact Strength
ISO 180/1A
+23°C
5.23
5.23
ftlb/in²
-30°C
2.47
3.19
ftlb/in²
-40°C
2.28
3.04
ftlb/in²
Thermal
dry
cond.
Unit
Test Norm
Heat Deflection Temperature
ISO 75-2/A
1.80 MPa, Unannealed
460
451
°F
0.45 MPa, Unannealed
495
491
°F
Melting Temperature
500
*
°F
ISO 11357-3
CLTE
ISO 11359-2
Flow : 23 to 55°C, 2.00 mm
32
*
E-6/K
Transverse : 23 to 55°C, 2.00 mm
115
*
E-6/K
Electrical
dry
cond.
Unit
Test Norm
Dielectric Strength (1.00 mm)
787
-
kV/in
IEC 60243
Injection
Value
Unit
Drying Temperature
176
°F
Drying Time
4
h
Rear Temperature
536 - 572
°F
Middle Temperature
536 - 572
°F
Front Temperature
536 - 572
°F
Nozzle temperature
536 - 572
°F
Processing (Melt) Temperature
536 - 572
°F
Mold Temperature
149 - 203
°F